Solar‐thermal Conversion Properties of Bilayered Porous Solar Absorbers fabricated by mixed halloysite/palygorskite clays

Nan Wang,Juan Jia,Wenxiao Mu,Hanxue Sun,Jiyan Li,Zhaoqi Zhu,Weidong Liang

DOI: https://doi.org/10.1002/ente.202300204

IF: 4.149

2023-05-27

Energy Technology

Abstract:In recent years, solar absorbers had received widespread attention, however, many absorbers were difficult to achieve large‐scale preparation, and the raw materials are expensive. Halloysite (HNTs) and palygorskite (PAL) have the advantage of abundant reserves and low prices. In this paper, solar absorbers with bilayer and porous features were prepared from mixed clays of HNTs and PAL, further studies focused on the solar‐thermal conversion efficiency of the absorbers. The mixed clays were gelated by aqueous polymerization of acrylamide (AM) and N, N'‐methylene bisacrylamide (MBA), then the surface of the gel was carbonized to obtain the double‐layer solar absorbers (F‐HNTs/PAL). The F‐HNTs/PAL shows excellent thermal stability with a weight‐loss ratio of 13% at 1000 °C, good mechanical property with a compressed strength of up to 200 KPa at 80% strain, abundant porosity with an adsorption pore volume of 0.057 cm3 g‐1, and low thermal conductivity (0.206 W m−1 K−1). Under 1 sun illumination, the F‐HNTs/PAL has a higher vapor rate of 1.215 kg m−2 h−1 that equals 84% solar‐to‐vapor efficiency, which is much more than 57% of F‐HNTs prepared by the same methods, but the F‐HNTs/PAL shows unique thermal stability and mechanical property. This article is protected by copyright. All rights reserved.

energy & fuels