Abstract:In this paper, the effect of thermomechanical treatment process on the hardening behavior, grain microstructure, precipitated phase, and tensile mechanical properties of the new high-strength and high-ductility Al-10.0Zn-3.0Mg-2.8Cu alloy was studied, and the optimal thermomechanical treatment process was established. The strengthening and toughening mechanisms were revealed, which provided technical and theoretical guidance for the engineering application of this kind of high strength-ductility aluminum alloy. Al-10.0Zn-3.0Mg-2.8Cu alloy cylindrical parts with external longitudinal reinforcement were prepared by a composite extrusion deformation process (reciprocal upsetting + counter-extrusion) with a true strain up to 2.56, and the organizational evolution of the alloys during the extrusion deformation process and the influence of pre-stretching treatments on the subsequent aging precipitation behaviors and mechanical properties were investigated. The results show that firstly, the large plastic deformation promotes the fragmentation of coarse insoluble phases and the occurrence of dynamic recrystallization, which results in the elongation of the grains along the extrusion direction, and the volume fraction of recrystallization reaches 42.4%. Secondly, the kinetic study showed that the decrease in the activation energy of precipitation increased the nucleation sites, which further promoted the diffuse distribution of the second phase in the alloy and a higher number of nucleation sites, while limiting the coarsening of the precipitated phase. When the amount of pre-deformation was increased from 0% to 2%, the size of the matrix precipitated phase decreased from 5.11 μm to 4.1 μm, and when the amount of pre-deformation was increased from 2% to 7%, the coarsening of the matrix precipitated phase took place, and the size of the phase increased from 4.1 μm to 7.24 μm. The finalized heat treatment process for the deformation of the aluminum alloy tailframe was as follows: solution (475 °C/3 h) + 2% pre-stretching + aging (120 °C/24 h), at which the comprehensive performance of the alloy was optimized, with a tensile strength of 634.2 MPa, a yield strength of 571.0 MPa, and an elongation of 15.2%. The alloy was strengthened by both precipitation strengthening and dislocation strengthening. After 2% pre-stretching, the fracture surface starts to be dominated by dense tough nest structure, and most of them are small tough nests, and small and dense tough nests are the main reason for the increase in alloy toughness after 2% pre-stretching deformation.

Enhanced formability and accelerated precipitation behavior of 7075 Al alloy extruded rod by high temperature aging

Effects of aging temperature on microstructure and high cycle fatigue performance of 7075 aluminum alloy

Effect of Aging Treatment on Microstructure and Mechanical Properties of As-Extruded AA6063 Aluminum Alloy

Effect of various non-isothermal aging on properties and microstructure of 7055 aluminum alloy

Extrusion Processing of High-Strength Al Alloy 7055

Effects of different initial states on dynamic tensile properties and microstructure of 7075 aluminum alloy

Influence of aging treatment on mechanical properties of 6061 aluminum alloy

Experimental study on cold forming process of 7075 aluminum alloy in W temper

Study on the Aging Precipitation Behavior and Kinetics of Al-10.0Zn-3.0Mg-2.8Cu Alloy by Pre-Deformation Treatment

Effect of ageing treatment process on the microstructure development and mechanical properties of 6082 Al alloy

A comparative study on cryogenic formability and paint baking property of AA7075 alloy sheets tempered at fast retrogressed and pre-aged conditions

Investigation of formability, microstructures and post-forming mechanical properties of heat-treatable aluminum alloys subjected to pre-aged hardening warm forming

Effect of Thermo-Mechanically Activated Precipitation on the Hot Deformation Behavior of High Strength Aluminum Alloy AA7075

Effects of aging treatment on the precipitation behaviors and mechanical properties of Al-5.0Mg-3.0Zn-1.0Cu cast alloys

Deformation Behavior and Mechanical Properties of AA7075 During Pre-hardened Aluminum Alloy Hot Forming Process

Precipitation behavior of spray-formed aluminum alloy 7055 during high temperature aging

Effect of heat treatment on some mechanical properties of 7075 aluminium alloy

Comparisons of Age Hardening and Precipitation Behavior in 7075 Alloy Under Single and Double-Stage Aging Treatments

Mechanical Properties and Microstructural Evolution of 6082 Aluminum Alloy with Different Heat Treatment Methods

Creep Aging Behavior of a Thermo-Mechanical Treated 7B04 Aluminum Alloy

Effect of Novel Thermomechanical Treatment on Microstructure and Properties of 6156 Alloy