Effect of conditions on wet carbonation products of recycled cement paste powder

Yuguang Mao,Pingping He,Sarra Drissi,Jian Zhang,Xiang Hu,Caijun Shi

DOI: https://doi.org/10.1016/j.cemconcomp.2023.105307

IF: 9.93

2023-09-29

Cement and Concrete Composites

Abstract:Wet carbonation is deemed a successful approach to recycling waste concrete powder. Controlling the growth and properties of products in the recycled cement paste powder (CPP) is highly dependent on the wet carbonation conditions. Therefore, this study aims to examine the effect of wet carbonation parameters on wet carbonation products in CPP. The wet carbonation of CPP resulted in mixed distribution of silica gel and CaCO 3 without significant layering on the CaCO 3 . In contrast, silica gel covered the outside of the CaCO 3 in the case of dry carbonation. Increasing the temperature from 25 °C to 80 °C promoted and accelerated the crystallization and growth of amorphous CaCO 3 , increased the crystallite size of CaCO 3 by 1.1–5.1 nm, and favored the formation of aragonite and vaterite; however, it also led to a significant crystal defect and/or distortion within CaCO 3 . Higher temperatures also promoted silica gel formation and increased its polymerization degree by 68.2%. On the other hand, increasing the CO 2 flow rate from 3 L/min to 5 L/min facilitated the crystallization and growth of CaCO 3 and contributed to the increase in the crystallite size of CaCO 3 by 3.0–6.6 nm. Higher CO 2 flow led to the incorporation of aluminum into silica gel and resulted in the transformation of its gel pores into capillary pores. The findings of this study contribute to a better understanding of the best experimental parameters to achieve a more efficient and effective concrete waste recycling process.

construction & building technology,materials science, composites