Jiwei Yao,Hui Yong,Yang Zhao,Chengyan Sun,Xianliu Xu,Baosheng Liu,Dongliang Zhao,Jifan Hu,Yanghuan Zhang
DOI: https://doi.org/10.1016/j.matchar.2023.113027
IF: 4.537
2023-05-25
Materials Characterization
Abstract:The Mg 90 Ce 5 Y 5 + x wt% ZnF 2 ( x = 3, 6, 10, 15) composites were prepared by mechanical ball-milling. The effects of ZnF 2 contents on the hydrogen absorption and desorption properties of Mg 90 Ce 5 Y 5 alloy were investigated by XRD, ICP-OES, TEM, PCT and DSC. The excellent hydriding-dehydriding characteristics of the samples after activation were attributed to the catalytic effect of the MgF 2 and MgZn 2 phases introduced in situ by the addition of ZnF 2 . The Mg 90 Ce 5 Y 5 + 6 wt% ZnF 2 composites exhibit the fastest hydrogen adsorption/desorption kinetics and lower decomposition temperatures. At 360 °C, 4.12 wt% H 2 can be absorbed within 180 s, and completely dehydrogenated within 740 s. In addition, the activation energy of dehydrogenation is reduced to 89.5 kJ/ mol, the optimal dehydrogenation temperature is reduced to 318 °C. It is due to the generation of in situ catalysts that weaken the MgH bond energy, refine the grain sizes, expand specific surface area and increase hydrogen diffusion paths. However, the improvement of the thermodynamics of the composites is limited, the enthalpy is 75.9 kJ/mol H 2 .
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing