Investigating of hydrolysis kinetics and catalytic mechanism of Mg–Ce–Ni hydrogen storage alloy catalyzed by Ni/Co/Zn-based MOF

Lin Zhang,Hui Yong,Shuai Wang,Zhihao Yan,Zhishun Xu,Yingjie Li,Baosheng Liu,Jifan Hu,Yanghuan Zhang

DOI: https://doi.org/10.1016/j.ijhydene.2024.05.357

IF: 7.2

2024-05-29

International Journal of Hydrogen Energy

Abstract:In this research, Mg 90 Ce 5 Ni 5 ingot alloys were prepared using the vacuum melting induction method. Subsequently, Ni/Zn/Co-based MOFs were synthesized via solvent thermal reaction. The phase composition and surface topography of the materials were tested using X-ray diffraction and scanning electron microscopy. The hydrogen production of Mg 90 Ce 5 Ni 5 alloy in MgCl 2 solution was studied. Avrami-Erofeev and Arrhenius's equations were utilized to fit the hydrogen production curve, studying hydrogen production kinetics and activation energy. The result shows that the alloy exhibits a faster initial hydrogen production rate after ball-milling, and the final hydrolysis yield is higher after hydrogenation. Compared to Mg 90 Ce 5 Ni 5 , Mg 90 Ce 5 Ni 5 + 2 wt% MOF/Ni, and Mg 90 Ce 5 Ni 5 + 2 wt% MOF/Zn, Mg 90 Ce 5 Ni 5 + 2 wt% MOF/Co demonstrates the best hydrolysis performance (1112 mL g −1 , activation energy of 12.9 ± 0.5 kJ mol −1 ). Due to the synergistic effect between CoO and MgH 2 , the absorption and release of hydrogen were promoted. The hydrogen production of the alloy after the introduction of MOF/Co reached 1730 mL g −1 , and the activation energy was 18.5 ± 1.4 kJ mol −1 . Optimizing the hydrolysis performance of the Mg 90 Ce 5 Ni 5 alloy was achieved by introducing a MOF catalyst through ball milling. This structure-performance relationship provides an efficient modification strategy for synthesizing magnesium alloys with excellent kinetics.

energy & fuels,electrochemistry,chemistry, physical