Abstract:In this work, we focused on studying the effects of TiO2 content and crystallization treatment on the elastic modulus of alkali-free aluminosilicate glass in the CaO–MgO–Al2O3–SiO2 (CMAS) system. Five groups of alkali-free CMAS parent glass with different TiO2 (0.30–1.50 wt%) components were designed, and several kinds of measurements including of Fourier-transform infrared spectrophotometer (FTIR), differential scanning calorimetry (DSC), x-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM) and elastic modulus tests were carried out to evaluate the performance of both parent glass and glass-ceramics samples. The results show the elastic modulus of alkali-free parent glass decreased gradually with the TiO2 content increased from 0.30 to 1.50 wt%, the maximum value of elastic modulus was 91.62 ± 0.80 GPa for T-1# sample (0.30 wt% TiO2) and it decreased to 77.99 ± 1.73 GPa for T-5# sample (1.50 wt% TiO2). The crystallization kinetics analysis of both T-1# and T-5# parent glass indicate the parent glass is in favor to surface crystallization. After the heat treatment at 1000–1150 °C for crystallization, the major crystal phase of both T-1# and T-5# group glass-ceramics was found to be anorthite (CaAl2Si2O8), with the crystal sizes around 200–500 nm. However, the crystallization treatments have shown different influence on the elastic modulus of T-1# and T-5# parent glass. The elastic modulus value of T-1# group glass-ceramics gradually decreased from 91.62 ± 0.80 GPa to 80.22 ± 2.84–90.82 ± 4.27 GPa after crystalized at 1000–1150 °C. On the contrary, the elastic modulus value of T-5# group glass-ceramics increased from 77.99 ± 1.73 GPa to 80.50 ± 4.57–88.91 ± 6.44 GPa after crystalized at 1000–1150 °C. This results further confirmed that the elastic modulus values of glass-ceramics main depends on the parent glass and the crystal phase in glass-ceramics.

Crystallization and mechanical properties of a barium titanosilicate glass

Crystallization kinetics and dielectric properties of barium strontium titanate based glass–ceramics

Phase Composition and Spectroscopic Characterization of Barium Titanate Containing Glass Ceramics

Dependence of Crystallization Behavior on Particle Size in Barium Strontium Titanate Glass‐Ceramics

Kinetic Behavior of the Nonisothermal Crystallization of Highly Refracted Glass Microspheres

Sintering of a Crystallizable K 2 O–CaO–SrO–BaO–B 2 O 3 –SiO 2 Glass with Titania Present

Crystallization and dielectric properties of oxyfluoride aluminosilicate glasses added with Na2O

High Glass Transition Temperature Barium Silicophosphate Glasses Designed with Topological Constraint Theory

Effect of the Ba/Ti Ratio on the Microstructures and Dielectric Properties of Barium Titanate‐Based Glass–Ceramics

Crystallization mechanism and ac conductivity studies on strontium barium niobate glass-ceramics

Elucidation of the crystallization behavior and the thermodynamics property of CuO/Bi12SiO20@ SiO2-B2O3-Bi2O3-CuO glass-ceramics

Sintering of a crystallizable K<sub>2</sub>O-CaO-SrO-BaO-B<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> glass with titania present

SiO2/Al2O3 ratio dependence of microstructures and dielectric properties in barium strontium titanate glass ceramics

Microstructure and mechanical properties of MgO–Al2O3–SiO2–TiO2 glass–ceramics

Crystallization of FeSiO3 in iron-containing sodium borosilicate glass

Crystal Nucleation and Growth in Li2O–Al2O3–SiO2 Base Glass Bulk

Crystallization mechanism and properties of CaO-B2O3-SiO2-Nb2O5 (CBSN) glass-ceramics

Effects of TiO2 content and crystallization treatments on elastic modulus of alkali-free aluminosilicate glass

A study on the crystallization of CaO–Al2O3–SiO2 system glasses

Effect of Crystallization of Cao-P2o5-Sio2-Mgo-F- Glass-Ceramics on Its Mechanical Properties

Crystallization of aluminosilicate glass with additive TiO2