Abstract:Pt1Cu1 NCs catalyst with abundant twin boundaries and high‐index facets displays outstanding catalytic activity for oxygen reduction reactions (ORR) due to the abundant effective active sites, low‐coordination numbers, and appropriate compressive strain. Meanwhile, the core‐shell and highly developed dendritic structures in Pt1Cu1 NCs catalyst give it an extremely high catalytic stability for ORR. Low‐coordination platinum‐based nanocrystals emanate great potential for catalyzing the oxygen reduction reactions (ORR) in fuel cells, but are not widely applied owing to poor structural stability. Here, several PtCu nanocrystals (PtCu NCs) with low coordination numbers were prepared via a facile one‐step method, while the desirable catalyst structures were easily obtained by adjusting the reaction parameters. Wherein, the Pt1Cu1 NCs catalyst with abundant twin boundaries and high‐index facets displays 15.25 times mass activity (1.647 A mgPt−1 at 0.9 VRHE) of Pt/C owing to the abundant effective active sites, low‐coordination numbers and appropriate compressive strain. More importantly, the core‐shell and highly developed dendritic structures in Pt1Cu1 NCs catalyst give it an extremely high stability with only 17.2% attenuation of mass activity while 61.1% for Pt/C after the durability tests (30 000 cycles). In H2‐O2 fuel cells, Pt1Cu1 NCs cathode also exhibits a higher peak power density and a longer‐term lifetime than Pt/C cathode. Moreover, theoretical calculations imply that the weaker adsorption of intermediate products and the lower formation energy barrier of OOH* in Pt1Cu1 NCs collaboratively boost the ORR process. This work offers a morphology tuning approach to prepare and stabilize the low‐coordination platinum‐based nanocrystals for efficient and stable ORR.

Multiscale Regulation of Ordered PtCu Intermetallic Electrocatalyst for Highly Durable Oxygen Reduction Reaction

Local Coordination and Ordering Engineering to Design Efficient Core-Shell Oxygen Reduction Catalysts

Engineering Porosity into Trimetallic PtPdNi Nanospheres for Enhanced Electrocatalytic Oxygen Reduction Activity

Multimetallic AuPd@Pd@Pt Core-Interlayer-shell Icosahedral Electrocatalysts for Highly Efficient Oxygen Reduction Reaction

Structurally Ordered Low‐Pt Intermetallic Electrocatalysts Toward Durably High Oxygen Reduction Reaction Activity

A Mesoporous Nanorattle‐Structured Pd@PtRu Electrocatalyst

Structure Evolution of PtCu Nanoframes from Disordered to Ordered for the Oxygen Reduction Reaction

Cuprous sulfide intermediate assisted synthesis of PtCu3 intermetallic electrocatalysts in multigram scale for oxygen reduction

Regulating Electrocatalytic Properties of Oxygen Reduction Reaction via Strong Coupling Effects between Co-NC Sites and Intermetallic Pt 3 Co

Hollow Porous Carbon-Confined Atomically Ordered PtCo 3 Intermetallics for an Efficient Oxygen Reduction Reaction

Synergistic Effect of Electrocatalyst for Enhanced Oxygen Reduction Reaction: Low Pt-Loaded CuPt Alloy Nanoparticles Supported on N-Doped Hierarchical Porous Carbon.

Regulating the Scaling Relationship for High Catalytic Kinetics and Selectivity of the Oxygen Reduction Reaction

Ordered Intermetallic PtCu Catalysts Made from Pt@Cu Core/Shell Structures for Oxygen Reduction Reaction

Highly‐Branched PtCu Nanocrystals with Low‐Coordination for Enhanced Oxygen Reduction Catalysis

Regulating the Surface Pt Coordination Environment in the PtN Overlayers on PtCuN Hollow Nanospheres for Efficient Oxygen Reduction Reaction

Electrochemical Synthesis of Monodispersed and Highly Alloyed PtCo Nanoparticles with a Remarkable Durability Towards Oxygen Reduction Reaction

Facile Synthesis of Structurally Ordered Low-Pt-loading Pd–Pt–Fe Nanoalloys with Enhanced Electrocatalytic Performance for Oxygen Reduction Reaction

Ordering‐dependent hydrogen evolution and oxygen reduction electrocatalysis of high‐entropy intermetallic Pt4FeCoCuNi

Intermetallic PtFe Electrocatalysts for the Oxygen Reduction Reaction: Ordering Degree-Dependent Performance.

Site-selective sulfur anchoring produces sintering-resistant intermetallic ORR electrocatalysts for membrane electrode assemblies

Facile Synthesis of Quaternary Structurally Ordered L12-Pt(Fe, Co, Ni)3 Nanoparticles with Low Content of Platinum As Efficient Oxygen Reduction Reaction Electrocatalysts.