Abstract:3D-printed carbon fiber composites hold significant potential in aerospace applications because of their lightweight, high strength and complex structure fabrication capabilities. However, additive manufacturing characteristics such as high porosity, anisotropy and continuous fiber content significantly affect the mechanical properties of printed parts. The aim of this study is to investigate the influence of hybrid printing of short and continuous carbon fibers on the mechanical properties and failure mechanisms of composites and to develop a model to predict elastic properties considering porosity. First, mechanical testing and characterization of short and continuous fiber reinforced polyamide (nylon) print filaments are performed. The results indicate that the elastic modulus and ultimate strength of continuous carbon fiber filaments reach 60 GPa and 1500 MPa, respectively, while the strength and elastic modulus of short carbon fiber filaments reach 60 MPa and 1 GPa, respectively. Then tensile specimens with different continuous fiber orientations and different continuous fiber placement sequences are printed and tested using a multi-material 3D printing technique. The specimens are characterized before and after testing using scanning electron microscopy and microscopy to assess the porosity and failure mechanisms of specimens with different configurations. The results show that the mechanical properties of the printed parts are much lower than those of the print filaments, which proves the serious negative impact of the material extrusion process on the mechanical properties of the printed structural parts. Finally, an analytical method for predicting the elastic behavior of printed composites is developed by introducing the porosity factor in the volume-averaged stiffness model. For continuous and short fiber filled composites with different fiber contents and printing orientations, the predicted results are in agreement with the experiments, and the prediction error is greatly reduced from 30% to less than 5%.

Influence of structural geometry on tensile properties and fracture toughness in 3D printed novel structures

Experimental and Theoretical Studies on 3D Printed Short and Continuous Carbon Fiber Hybrid Reinforced Composites

Effect of infill density and reinforced perimeters on tensile properties and fracture mechanism of 3D printing carbon fiber–reinforced composite

Structural influences of two-dimensional and three-dimensional carbon/epoxy composites on mode I fracture toughness behaviors with rate effects on damage evolution

Research into Specific Mechanical Properties of Composites Produced by 3D-Printing Additive Continuous-Fiber Fabrication Technology

Process evaluation, tensile properties, mathematical models, and fracture behavior of 3D printed continuous fiber reinforced thermoplastic composites

Evolution of microstructure and thermo‐mechanical attributes of fiber reinforced polyamide during fused deposition modeling 3D printing: A comprehensive characterization study

An Investigation of Tensile, Fatigue, and Fracture Behavior of 3D-Printed Polymers

An investigation into mechanical properties of a 3D printed two-matrix continuous fiber composites with multi-cavity structure

Compressive properties and failure mechanisms of 3D-printed continuous carbon fiber-reinforced auxetic structures

Mechanical Performance and Failure Analysis of a 3D-Printed "Continuous Layer–Lattice Layer–Continuous Layer" Sandwich Structure

Mechanical properties and damage failure of 3D‐printed continuous carbon fiber‐reinforced composite honeycomb sandwich structures with fiber‐interleaved core

Effect of the Thickness on the Fracturing Behavior of Discontinuous Fiber Composite Structures

Experimental Characterization and Analysis of the In-Plane Elastic Properties and Interlaminar Fracture Toughness of a 3D-Printed Continuous Carbon Fiber-Reinforced Composite

Crack modes and toughening strategies of bioinspired 3D printed double-helicoidal architectures

Effects of Geometrical and Mechanical Properties of Fiber and Matrix on Composite Fracture Toughness

Discontinuous fibrous Bouligand architecture enabling formidable fracture resistance with crack orientation insensitivity

ANISOTROPIC IMPACT TOUGHNNESS OF CHOPPED CARBON FIBER REINFORCED NYLON FABRICATED BY MATERIAL-EXTRUSION-BASED ADDITIVE MANUFACTURING

Strain rate dependence of 3D printed continuous fiber reinforced composites

Elastic and Fracture Behavior of Three-Dimensional Ply-to-Ply Angle Interlock Woven Composites: Through-Thickness, Size Effect, and Multiaxial Tests

Failure of 3D-printed composite continuous carbon fiber hexagonal frames