An efficient far‐red emission Sr 2 InSbO 6 :Mn 4+ , M (M = Li + , Na + , and K + ) phosphors for plant cultivation LEDs
Yan Xie,Xue Geng,Yuan Wang,Jiang Guo,Yuhui Lu,Qiuyi Lv,Zhijiang Ma,Dan zhang,Jin Zhao,Bin Deng,Ruijin Yu
DOI: https://doi.org/10.1111/jace.18115
IF: 4.186
2021-09-21
Journal of the American Ceramic Society
Abstract:High-efficiency and far-red light phosphors based on Mn4+-doped inorganic luminescence materials are beneficial to plant cultivation. However, Mn4+-doped oxide phosphors have a common problem of low quantum efficiency. Alkali metal ion co-doping can effectively improve the luminescence properties of Mn4+-activated oxide phosphors. Herein, a series of Sr2InSbO6:Mn4+, M (SISO:Mn4+, M) (M = Li+, Na+, and K+) far-red-emitting phosphors co-doped alkali metal ions were firstly synthesized. Density functional theory calculation indicated that SISO is a kind of indirect band-gap material with a band-gap of ∼1.60 eV. The SISO:Mn4+ samples showed a far-red light at 698 nm upon 365 nm, which perfectly matched the absorption spectrum of the far-red-phytochrome (Pfr) of plants. The doping concentration of the SISO:Mn4+ samples was optimized to be 0.006 mol. The concentration quenching mechanism was defined as dipole-dipole interaction by combining the Dexter theory and the Inokuti-Hirayama model. Optimizing the sintering temperature and co-doped with alkali metal ions (Li+, Na+, and K+) could improve the luminescent intensity of SISO:Mn4+. The optimum sintering temperature was 1300 °C. The IQE of SISO:0.006Mn4+ and SISO:0.006Mn4+, 0.006Li+ phosphors are 22.67% and 60.56%, respectively. SISO:Mn4+, Li+ phosphors based plant growth LEDs demonstrate excellent optical stability and long lifetime. Thus, these phosphors are promising candidates for plant cultivation LEDs.This article is protected by copyright. All rights reserved
materials science, ceramics