Synthesis of Eu3+ doped magnesium aluminate spinel via combustion method: Investigation of thermodynamics, crystal structure, microstructure, and luminescence properties

Mehran Ghodrati,Seyed Mahdi Rafiaei

DOI: https://doi.org/10.1002/jccs.202400155

2024-09-20

Journal of the Chinese Chemical Society

Abstract:MgAl2O4:Eu3+ were produced by combustion method. FE‐SEM, X‐ray and FT‐IR analyses confirmed the successful formation of spinels. It was observed that the addition of large amounts of Eu3+ suppress the crystallinity. Photoluminescence characterization showed that via monitoring at 356 nm, doping MgAl2O4 with 7 wt% Eu3+ compared to other synthesized materials, provide the most intense emission properties at 592 nm. In the current research, the rare earth‐doped magnesium aluminate (MgAl2O4:Eu3+) spinels were produced by the combustion synthesis method. The employment of thermodynamic calculations revealed that the combustion approach is a proper way to synthesize MgAl2O4:Eu3+ material by urea fuel, although this procedure was fulfilled at 500°C, the final temperature will be around 2030°C. The x‐ray and FT‐IR spectra confirmed the successful formation of spinels, while it was shown that the calcination procedure results in a significant increase of crystallinity. On the other hand, it was interestingly seen that the addition of large amounts of Eu3+dopant (10 wt%) suppresses the crystallinity. The MAUD calculations interestingly revealed that the increase of Eu3+ dopant from 1 to 10 wt% leads to the increase of MgO and Al2O3 impurities. The related microstructural evaluations revealed that the particle size of the synthesized powders is mostly less than 40 nm which shows the superiority of combustion synthesis over other commercial methods. Also, the broadening of XRD peaks confirmed the formation of nano‐sized powder. The photoluminescence (PL) characterizations showed that doping of MgAl2O4 with 7 wt% Eu3+ brings the most intensive emission properties at the wavelengths of 592 and 617 nm.

chemistry, multidisciplinary