Abstract:Hydrogen-free a-C/a-C:Ti nanomultilayer (a-C NM) films were deposited on medical Ti6Al4V by the magnetron sputtering technique under bias-graded voltage. Cell tests and implantations were performed for the a-C NM films coated Ti6Al4V with the uncoated Ti6Al4V as the control. The canine total hip arthroplasty (THA) surgeries were conducted for 12 dogs using the coated femoral heads, with the CoCr heads as the control. Results of cell tests showed that the coated Ti6Al4V had no cytotoxicity, and there was no statistical difference of the cell attachment rates between the coated and uncoated sample (P = 0.091). No significant difference of the tissue response around the coated and uncoated implants were observed after the intramuscular (P = 0.679) and intraosseous implantations (P = 0.122). After two years of successful canine THA, the polyethylene wear particles isolated from periprosthetic soft tissue showed similar sizes, shapes and counts in the two groups (all of the P values >0.05). The retrieved femoral heads showed slightly change of the surface roughness, but no statistical differences between groups (P = 0.696). However, the systemic metal ion analysis indicated that the content of Co and Cr ions released in the coated group (Co: 0.71 ± 0.06 μg/L, Cr: 0.52 ± 0.05 μg/L) were significant lower than that in the control (Co: 1.98 ± 0.16 μg/L, Cr: 1.17 ± 0.19 μg/L) (both P < 0.005). Histological analysis of the periprosthetic tissue in CoCr group showed a severer histiocyte response than that in the coated group (P = 0.029). The head-taper interfaces showed galvanic corrosion attack in the CoCr group, but not in the coated Ti6Al4V group. Therefore, the a-C NM films coated Ti6Al4V exhibited good biocompatibility as an implant material. Compared with the CoCr, the coated Ti6Al4V femoral head could provide comparable in vivo wear properties, release less harmful metal ions and reduce the inflammatory response in periprosthetic tissue, which may help to prolong the longevity of prostheses.

Fabrication of TC4/TiCp New Hip Prosthesis by Laser Cladding

Mechanical Tests, Wear Simulation and Wear Particle Analysis of Carbon-Based Nanomultilayer Coatings on Ti6Al4V Alloys As Hip Prostheses

In-situ Synthesized TiC/TiB Ceramic Particle Composite Coating by Laser Cladding on TC4 Titanium Alloy

Microstructure analysis and wear behavior of titanium cermet femoral head with hard TiC layer.

Laser Surface Coating of Re Bioceramic Layer on Tc4

Increasing the wear resistance of hip prostheses components using micro-nanostructured thin layers

Evaluation of microstructure, mechanical properties and osseointegration capacity of laser cladding β-type TiNbZr coatings

DLC coating over pre-oxidized and textured Ti6Al4V for superior adhesion and tribo-performance of hip implant

Microstructure and Wear Resistance of TiCp/Ti6Al4V Composite Coatings by Follow-Up Ultrasonic-Assisted Laser Additive Manufacturing

Fabrication of dense α-alumina layer on Ti-6Al-4V alloy hybrid for bearing surfaces of artificial hip joint

Investigating the performance of tricalcium phosphate bioceramic reinforced with titanium nanoparticles in friction stir welding for coating of orthopedic prostheses application

Development and characterization of Ni60 alloy and SiC ceramic reinforced metal matrix composite coating on Ti-6Al-4V using laser cladding with coaxial powder feeding system

In situ Ti 2 Ni/Ti 2 S reinforced Ti-based composites with enhanced mechanical properties fabricated by laser cladding on TC4 alloy

Microstructure and wear resistance of laser clad composite coating on TC4 titanium alloy surface

Mechanical and Corrosion Properties of Laser Surface-Treated Ti13Nb13Zr Alloy with MWCNTs Coatings

Research on the in Situ Fabrication of Bioceramic Composite Coatings by Laser Cladding

In Vitro and in Vivo Investigations of A-C/a-c:Ti Nanomultilayer Coated Ti6Al4V Alloy As Artificial Femoral Head.

Fabrication of Tic Reinforced Ni Based Coating by Laser Cladding

Multi-ceramic phases synergistically reinforced titanium matrix composite coating deposited by laser cladding: Effect of B 4 C content on the microstructure and wear properties

High-performance bioceramic coatings of 3D printed titanium alloys via FS-auxiliary micro-arc oxidation manufacturing

Effect of SiC and TiC content on microstructure and wear behavior of Ni-based composite coating manufactured by laser cladding on Ti-6Al-4V