An Inorganic‐Rich Solid Electrolyte Interphase for Advanced Lithium‐Metal Batteries in Carbonate Electrolytes

Sufu Liu,Xiao Ji,Nan Piao,Ji Chen,Nico Eidson,Jijian Xu,Pengfei Wang,Long Chen,Jiaxun Zhang,Tao Deng,Singyuk Hou,Ting Jin,Hongli Wan,Jingru Li,Jiangping Tu,Chunsheng Wang

DOI: https://doi.org/10.1002/anie.202012005

2020-12-16

Angewandte Chemie International Edition

Abstract:In carbonate electrolytes, the organic‐inorganic solid electrolyte interphase (SEI) formed on the lithium (Li) metal anode surface is strongly bonded to Li and experiences the same volume change as Li, thus it undergoes continuous cracking/reformation during plating/stripping cycles. Here, an inorganic‐rich SEI is designed on a Li metal surface to reduce its bonding energy with Li metal by dissolving 4 M concentrated LiNO 3 in dimethyl sulfoxide (DMSO) as an additive for a fluoroethylene carbonate (FEC) based electrolyte. Due to the aggregate structure of NO 3 ‐ ions and its participation in the primary Li + solvation sheath, abundant Li 2 O, Li 3 N, and LiN x O y grains are formed in the resulting SEI, in addition to the uniform LiF distribution from the reduction of PF 6 ‐ ions. The inorganic‐rich SEI's weak bonding (high interface energy) to Li can effectively promote Li diffusion along the SEI/Li interface and prevent Li dendrite penetration into the SEI. As a result, our designed carbonate electrolyte enables a Li anode to achieve a high Li plating/stripping CE of 99.55% (1 mA cm ‐2 , 1.0 mAh cm ‐2 ) and the electrolyte also enables a Li||LiNi 0.8 Co 0.1 Mn 0.1 O 2 (NMC811) full cell (2.5 mAh cm‐2) to retain 75% of its initial capacity after 200 cycles with an outstanding CE of 99.83%. The concentrated additive strategy presented here provides a drop‐in practical solution to further optimize carbonate electrolytes for beyond Li‐ion batteries.

chemistry, multidisciplinary