Surface-Functionalized Coating for Lithium-Rich Cathode Material To Achieve Ultra-High Rate and Excellent Cycle Performance
Yanying Liu,Zhe Yang,Jianjian Zhong,Jianling Li,Ranran Li,Yang Yu,Feiyu Kang
DOI: https://doi.org/10.1021/acsnano.9b05960
IF: 17.1
2019-09-23
ACS Nano
Abstract:Although the lithium-rich cathode material Li<sub>1.2</sub>Mn<sub>0.54</sub>Ni<sub>0.13</sub>Co<sub>0.13</sub>O<sub>2</sub>, as a promising cathode material, has a high specific capacity, it suffers from capacity decay and discharge voltage decay during cycling. In this work, the specific capacity and discharge voltage of Li<sub>1.2</sub>Mn<sub>0.54</sub>Ni<sub>0.13</sub>Co<sub>0.13</sub>O<sub>2</sub> are stabilized by surface-functionalized LiCeO<sub>2</sub> coating. We have conducted LiCeO<sub>2</sub> coating <i>via</i> a mild synchronous lithium strategy to protect the electrode surface from electrolyte attack. This optimized LiCeO<sub>2</sub> coating has high Li<sup>+</sup> conductivity and abundant oxygen vacancies. The results demonstrate that 3% LiCeO<sub>2</sub>-coated Li<sub>1.2</sub>Mn<sub>0.54</sub>Ni<sub>0.13</sub>Co<sub>0.13</sub>O<sub>2</sub> exhibits the highest capacity retention rate at 1, 2, and 5 C after 200 cycles, which were 84.3%, 85.4%, and 86.3%, respectively. The discharge specific capacity was almost 1.3, 1.4, and 1.4 times that of the pristine electrode. In addition, the 3% LiCeO<sub>2</sub> electrode exhibited the least voltage decay of 0.409, 0.497, and 0.494 V at 1, 2, and 5 C, which was only about half of the pristine electrode. It should not be overlooked that the 3% LiCeO<sub>2</sub> electrode still exhibits a high capacity at high current densities of 1250 mA g<sup>–1</sup> (5 C) and 2500 mA g<sup>–1</sup> (10 C), and its specific discharge capacities are 190.5 and 160.6 mAh g<sup>–1</sup>, respectively. These outstanding electrochemical properties benefit from surface-functionalized LiCeO<sub>2</sub> coatings. To better understand the mechanism of oxygen loss of lithium-rich materials, we propose the lattice oxygen migration path of the LiCeO<sub>2</sub>-coated electrodes during the cycle. Our research provides a possible solution to the poor rate capability and cycle performance of cathode materials through surface-functionalized coatings.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology