Synthesis and Physicochemical Characterization of Solid Oxide Electrolyte and Electrode Materials for Medium-Temperature Fuel Cells

M. V. Kalinina,I. G. Polyakova,S. V. Myakin,T. V. Khamova,L. N. Efimova,I. Yu. Kruchinina

DOI: https://doi.org/10.1134/s0036023623603173

2024-07-18

Russian Journal of Inorganic Chemistry

Abstract:Xerogels and finely dispersed СeO 2 –Nd 2 O 3 and Gd 2 O 3 –La 2 O 3 –SrO–Ni(Co) 2 O 3–δ mesoporous powders are synthesized by cocrystallization of the corresponding nitrate solutions with ultrasonic treatment, and used to prepare nanoceramic materials with a fluorite-like and orthorhombic perovskite crystal structures, respectively, with CSRs of ca. 55–90 nm (1300°C). The physicochemical characterization of the prepared ceramic materials revealed an open porosity of 7–11% for СeO 2 –Nd 2 O 3 ceramics and 17–42% for Gd 2 O 3 –La 2 O 3 –SrO–Ni(Co) 2 O 3–δ ceramics. Cerium oxide-based materials possess a predominantly ionic electrical conductivity with σ 700°С = 0.31 × 10 –2 S/cm (the ion transference number t i = 0.71–0.89 in the temperature range 300–700°C) due to the formation of mobile oxygen vacancies upon heterovalent substitution of Nd 3+ for Се 4+ . Solid solutions based on gadolinium nickelate and gadolinium cobaltite feature a mixed electronic–ionic conductivity (σ 700°С = 0.59 × 10 –1 S/cm) with the electron and ion transference numbers t e = 0.92–0.99 and t i = 0.08–0.01. The prepared ceramic materials are shown to be promising as solid oxide electrolytes and electrodes for medium-temperature fuel cells.

chemistry, inorganic & nuclear