Abstract:The multistage microporous electrocatalysts to assist the energy-efficient hydrogen generation from water electrolysis were fabricated on the surface of three-dimensional porous foam (NF) by a one-step hydrothermal synthesis strategy. When the molar ratio of sulfur to phosphorus in the initial mixed solution was 1:1, an amorphous P-doped nickel-based sulfide (NiSP/NF) electrocatalyst, with Ni3S2 and NiPS3 as the main and secondary crystalline phase, respectively, was obtained by hydrothermal treatment at 120 degrees C for 24 h. Thanks to its unique bi-hierarchy microporous structure composed of interwoven interconnected ultra-thin nanosheets, yielding the nearly 14-fold increased electrochemical active surface area (ECSA), sufficient active sites and interface channels are provided for hydrogen evolution reaction (HER) during water splitting. Meanwhile, benefiting from the lattice defects created by crystalline Ni3S2 and the strong electronic interactions with crystalline P doping phases, respectively, the intrinsically catalytic activity of nickel-based electrocatalyst was significantly enhanced. The synergistic effects enable NiSP/NF to exhibit remarkable performances during the whole water splitting, achieving a current density of 10 mA center dot cm(-2) in 1 mol center dot L-1 KOH solution with overpotentials for HER and OER as low as 67 and 212 mV, respectively. Assembled as an electrolyzer for overall water splitting (OWS), a current density of 100 mA center dot cm(-2) can be achieved only needing a cell voltage of 1.878 V, even at 500 mA center dot cm(-2) the needed cell voltage was only 2.558 V for NiSP/NF, which is dramatically superior to noble metal catalysts and helpful to improve hydrogen production efficiency for water electrolysis. Particularly, as a bifunctional electrocatalyst, NiSP/NF also exhibited excellent long-term stability and durability, because of less than a 0.03 V cell voltage increase after running a 120-hour chronopotentiometric test at 500 mA center dot cm(-2).

High‐Performance Bifunctional Ni−Fe−S Catalyst in situ Synthesized within Graphite Intergranular Nanopores for Overall Water Splitting

Confined synthesis of highly dispersed Ni anchored on mesoporous carbon as efficient catalyst for water splitting

In Situ Formation of Cobalt Nitrides/Graphitic Carbon Composites As Efficient Bifunctional Electrocatalysts for Overall Water Splitting

Sulfur vacancies promoting Fe-doped Ni<sub>3</sub>S<sub>2</sub>nanopyramid arrays as efficient bifunctional electrocatalysts for overall water splitting

Sulfur Vacancies Promoting Fe-Doped Ni(3)S(2)Nanopyramid Arrays As Efficient Bifunctional Electrocatalysts For Overall Water Splitting

Fe7S8/N-doped Graphene Foam Composite as Efficient Bifunctional Electrocatalysts for Overall Water Splitting

Self-Supportive Mesoporous Ni/Co/Fe Phosphosulfide Nanorods Derived from Novel Hydrothermal Electrodeposition As a Highly Efficient Electrocatalyst for Overall Water Splitting.

Fluorine-doped Nickel Cobalt Oxide Spinel As Efficiently Bifunctional Catalyst for Overall Water Splitting

A Highly Efficient Fe-doped Ni3S2 Electrocatalyst for Overall Water Splitting

Highly efficient sulfur-doped Ni3Fe electrocatalysts for overall water splitting: Rapid synthesis, mechanism and driven by sustainable energy

FeCoNiS Nanoparticles Integrated with Nitrogen−Doped Vertically Oriented Graphene via Single−Step Electrodeposition: An Efficient Bifunctional Catalyst for Overall Water Splitting

In situ fabrication of Ni3S2/Cu2S heterojunction on nickel foam as a highly efficient and durable electrocatalyst for overall water splitting

Self-supporting Amorphous Nanoporous NiFeCoP Electrocatalyst for Efficient Overall Water Splitting

Iron, Tungsten Dual‐Doped Nickel Sulfide as Efficient Bifunctional Catalyst for Overall Water Splitting

S-doped Ni(Fe)OOH bifunctional electrocatalysts for overall water splitting

Synergistic Coupling of Ni Nanoparticles with Ni3 C Nanosheets for Highly Efficient Overall Water Splitting

Multistage Microporous Bifunctional Catalyst Constructed by P-doped Nickel-Based Sulfide Ultra-Thin Nanosheets for Energy-Efficient Hydrogen Production from Water Electrolysis

A Heterostructure Coupling of Exfoliated Ni–Fe Hydroxide Nanosheet and Defective Graphene as a Bifunctional Electrocatalyst for Overall Water Splitting

Highly efficient overall-water splitting enabled via grafting boron-inserted Fe-Ni solid solution nanosheets onto unconventional skeleton

Promotion of Overall Water Splitting Activity Over a Wide pH Range by Interfacial Electrical Effects of Metallic NiCo-nitrides Nanoparticle/NiCo2O4 Nanoflake/graphite Fibers.

Partially Oxidized Ni Nanoparticles Supported on Ni-N Co-Doped Carbon Nanofibers As Bifunctional Electrocatalysts for Overall Water Splitting