Robust cellulose-carbon nanotube conductive fibers for electrical heating and humidity sensing

Jianhua Ma,Haihong Pu,Pengxin He,Qiangli Zhao,Shaoxue Pan,Yaowu Wang,Chen Wang

DOI: https://doi.org/10.1007/s10570-021-04026-y

IF: 6.123

2021-06-22

Cellulose

Abstract:Multifunctional fibers have attracted widespread attention due to applications in flexible smart wearable devices. However, simultaneously obtaining a strong and functional woven fiber is still a great challenge owing to the conflict between the properties mentioned above. Herein, mechanically strong and highly conductive cellulose/carbon nanotube (CNT) composite fibers were spun using an aqueous alkaline/urea solution. The microstructure as well as physical properties of the resulting fibers were characterized via scanning electron microscopy, infrared spectroscopy, mechanical and electrical measurement. We demonstrated that carboxylic CNTs can be well dispersed in alkali/urea aqueous systems which also dissolved cellulose well. The subsequent wet spinning process aligned the CNTs and cellulose molecules inside the regenerated composite fiber well, enhancing the interaction between these two components and endowing the composite fiber having a 20% CNT loading with an excellent mechanical strength of 185 MPa. Benefiting from the formation of conductive paths, the composite fiber with the diameter of about 50 μm possessed an electrical conductivity value in the range of 64–1274 S/m for 5–20 wt% CNT loading. This excellent mechanical strength and high electrical conductivity enable the composite fiber to exhibit a great potential in joule heating; the heating temperature of cellulose/CNT-20 fiber reached more than 55 °C within 15 s at 9 V. In addition, the multifunctional filaments are further manufactured as a water sensor to measure humidity. This work provides a potential material that can be applied in the fields of wearable electronics and smart flexible fabrics.

materials science, textiles,polymer science, paper & wood

What problem does this paper attempt to address?

This paper aims to address the problem of manufacturing environmentally friendly conductive fibers that are both strong and functional. Researchers successfully prepared cellulose/CNT composite fibers with high mechanical strength and excellent electrical conductivity by combining carboxylated carbon nanotubes (CNTs) with cellulose and using a water-soluble alkaline/urea solution for wet spinning. These fibers have good microstructure and physical properties, and their conductivity and mechanical strength make them potential candidates for electric heating and humidity sensing. Despite the limitations of functional particle aggregation and poor interface characteristics with the cellulose matrix in previous attempts, the researchers were able to achieve effective dispersion of CNTs and enhance their interaction with cellulose by acid treatment and using a NaOH/urea dissolution system. Experimental results showed that the composite fibers with 20% CNTs exhibited high mechanical strength of 185 MPa and conductivity as high as 1274 S/m, enabling them to be used for electric heating with a temperature increase of over 55°C within 15 seconds under a 9 V voltage. Furthermore, these multifunctional fibers can also be used as humidity sensors. This work provides possibilities for developing new materials for flexible wearable electronic devices and smart textiles.