Abstract:To synergistically improve the strength-ductility of copper alloys used in the miniaturized component, Cu-3.2Ti-0.2Fe-0.2V alloy with heterogeneous structure was obtained by thermo-mechanical treatment (namely, short-time annealing). The heterogeneous structure was composed of the non-uniform grains formed due to Laves phase inhibiting grain growth and FCC structured Cu4Ti phase with good coherent interface precipitated on the grain boundaries in sub-micro size. After aging at 400 °C for 2 h and then 450 °C for 4 h, the ultimate tensile strength and elongation of the heterogeneous-structured alloy were 976.8 MPa and 18.8% respectively, which was approximately 120 MPa more than that of the coarse-grained alloy after complete annealing, but both alloys had comparable ductility. When cold-rolling with 5% reduction was carried out before the aging of 450 °C, the strength increased to 1057 MPa and corresponding elongation was still over 10%. The strengthening mechanism of alloy with heterogeneous structure was analyzed and the hetero-deformation induced hardening of 284.5 MPa was the other significant reinforcement. The semi in-situ observation of tensile deformation behavior shown that the superior ductility in coarse-grained alloy was mainly attributed to the slipping and twinning. While grain rotation and grain boundary sliding were additional deformation mechanism in heterogeneous-structured alloy during tensile deformation, meanwhile, the texture of S, {110}<1 1 ‾ 1> and {331}<1 2 ‾ 3> components converted to the texture of {441}< 1 ‾ 1 ‾ 8>, Goss, Copper and {012}< 8 2 ‾ 1 > components. The deteriorative ductility after rolling with the reduction of 5% was owing to the S and Cube components converted to the strong texture of {032}<22 3 ‾ > components.

Microstructure and mechanical properties of Cu-Ti alloy by mechanical alloying

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Microstructure Characterization of the Cu-Ti-C Composites Prepared by Mechanical Alloying and Spark Plasma Sintering

Microstructure and Mechanical Properties of a High-Strength Ti-4Al-2Fe-3Cu Alloy Fabricated by Sintering and Hot Extrusion

Mechanical milling and its influence on microstructure and electric conductivity of high mass fraction TiC / Cu composites

Eff ects of Diff erent Mechanical Alloying Parameters on Microstructure of High Temperature Nanocrystalline Cu-Ta Alloys

Microstructures and mechanical properties of Cu–Ti alloys with ultrahigh strength and high ductility by thermo-mechanical treatment

Microstructure and mechanical properties of Cu-12 Al-6 Ni with Ti addition prepared by powder metallurgy

Microstructure Evolution and Mechanical Properties of PM-Ti43Al9V0.3Y Alloy

Study on Mechanical Properties and Microstructure of Cu20Fe80 Alloy Using the Mechanical Alloying

Study on Microstructure and Properties of Cu-Zr Alloy Prepared by Mechanical Alloying

Fabrication of High Strength Conductivity Submicron Crystalline Cu-5%Cr Alloy by Mechanical Alloying

Microstructure and Mechanical Properties of Ti–V–Al–Cu Shape Memory Alloy by Tailoring Cu Content

Effect of micro-alloying element Ti on mechanical properties of Cu–Cr alloy

Microstructures and mechanical properties of high strength Ti-XAl-2Fe-3Cu alloys fabricated by powder compact extrusion

Microstructure, Mechanical and Tribological Properties of Cu40Zn-Ti3AlC2 Composites by Powder Metallurgy

A Novel Microstructure of Cu-Ti Alloy with Ultrahigh Electrical Conductivity and Strength

Effect of Mechanical Alloying on the Microstructure and Properties of W–Ti Alloys Fabricated by Spark Plasma Sintering

Effect of Ti content on microstructures and mechanical properties of cast Al-2Li-2Cu-0.5Mg alloy

Structure and properties of the mechanically alloyed Cu-5Cr alloy

Effect of Cu–Al Ratio on Microstructure and Mechanical Properties of Cu–Al Alloys Prepared by Powder Metallurgy