Nickel-cobalt layered double hydroxide cathode materials with excellent cycle stability for nickel-metal hydride batteries

Min Jiang,Yunfeng Zhu,Yana Liu,Jiguang Zhang,Yao Zhang,Yicheng Sun,Peng Zeng,Jie Hou,Yuke Ren,Zhixin Ba,Liquan Li
DOI: https://doi.org/10.1016/j.jallcom.2023.168980
IF: 6.2
2023-01-22
Journal of Alloys and Compounds
Abstract:Nickel-cobalt layered double hydroxides (Ni-Co LDHs) with different Ni/Co molar ratios (3:1, 4:1 and 5:1) are synthesized by a simple and effective one-step solvothermal method and then are used as cathode materials for nickel-metal hydride (Ni-MH) batteries. In comparison with the Ni(OH) 2 , the Ni-Co LDHs electrodes display higher discharge capacity and excellent cycling stability, especially the electrode with a Ni/Co molar ratio of 4:1 (NC 2). The NC 2 electrode obtains a maximum discharge capacity of 356.2 mAh/g at the discharge rate of 200 mA/g, and delivers a high capacity retention of 99.1% after 200 cycles. The results of microstructure characterization reveal that the Ni-Co LDHs exhibit a unique three-dimensional flower-like morphology and the enlarged interlayer spacing, which can promote ion transmission and charge transfer. In addition, the excellent structural stability of the Ni-Co LDHs and Co-Co LDHs in the KOH alkaline electrolyte and the synergies between them may also be essential for the improvement of electrochemical performances. The present work provides valuable information to explore a promising cathode material for the advanced nickel-metal hydride batteries.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
This paper attempts to solve several key problems existing in traditional β - Ni(OH)₂ as a cathode material in nickel - metal hydride batteries (Ni - MH): 1. **Poor conductivity**: The conductivity of β - Ni(OH)₂ is not good, which limits its application under high - rate charge - discharge conditions. 2. **Capacity close to theoretical value**: The specific capacity of β - Ni(OH)₂ is already close to its theoretical value, and there is limited room for further improvement. 3. **Poor over - charge stability**: Under over - charge conditions, β - Ni(OH)₂ is easily converted into γ - NiOOH and cannot be completely restored to β - Ni(OH)₂ during the discharge process, resulting in a decrease in discharge capacity. 4. **Poor cycle stability**: After long - term cyclic use, the structural stability of β - Ni(OH)₂ is relatively poor, leading to capacity attenuation. In order to solve the above problems, the authors synthesized nickel - cobalt layered double hydroxides (Ni - Co LDHs) with different Ni/Co molar ratios and used them as cathode materials for Ni - MH batteries. Through experimental research, it was found that Ni - Co LDHs, especially the sample with a Ni/Co molar ratio of 4:1 (NC 2), exhibited the following advantages: - **Higher discharge capacity**: The NC 2 electrode has a maximum discharge capacity of 356.2 mAh/g at a discharge rate of 200 mA/g, which is much higher than that of traditional β - Ni(OH)₂. - **Excellent cycle stability**: The NC 2 electrode can still maintain a capacity retention rate of 99.1% after 200 cycles. - **Good high - rate performance**: The NC 2 electrode exhibits a relatively high discharge capacity at different discharge rates, especially under high - rate conditions. - **Unique three - dimensional flower - like structure**: This structure is conducive to the transport of electrolyte ions and charge transfer, thereby improving electrochemical performance. - **Structural stability**: Ni - Co LDHs has excellent structural stability in KOH alkaline electrolyte, which helps to improve the overall performance of the battery. In summary, this paper successfully solves the problems existing in traditional cathode materials by synthesizing Ni - Co LDHs and applying them to Ni - MH batteries, and provides a new direction for the development of high - performance Ni - MH batteries.