Abstract:Several commercial ceramic resins are nowadays available in the market of Additive Manufacturing, making more approachable ceramic stereolithography (CS) to an extended audience of users, from academic to industrial fields. Lack of knowledge in terms of material characterization and expected behavior in the manufacturing process are the main problems that involve difficulties in obtaining precise, dense, resistant, and crack-free ceramic parts. This article presents a characterization of a porcelain-based commercial ceramic resin for digital light processing (DLP), Porcelite® by Tethon 3D, and a study on the printing dimensional accuracy and cracks formation in sintered samples in dependence on the process parameters used have been performed. Two different Porcelite® resins with different solid loadings are available in the market. Rheological measurements, thermogravimetry combined with differential thermal analysis, field emission scanning electron microscopy observation, and X-ray diffraction allowed the complete characterization of the most loaded ceramic suspension. A design of experiment (DoE) approach led to planning the experimental work identifying the geometry of the samples, the process parameters, and their levels of variation to evaluate the aspects that influence dimensional accuracy when printing and crack formation during thermal treatment. The final volumetric shrinkage of components produced, respectively, with Porcelite® Bison (PB) and Porcelite® Universal (PU) is 19.3 ± 2.2% and 41.1 ± 3.6%. Solid loadings evaluated through TG–DTA are 52 wt% for PU and 72 wt% for PB. Statistical analyses highlight that layer thickness and degree of exposure influence accuracy in x- and y-directions, and for both resins, part thickness influences accuracy only in the x-direction for PB resin. Layer thickness, part thickness, and interaction are influential in the z-direction. The printed accuracy shows certain independence from the resin solid loading.

Synergistic regulation of sintering temperature in calcium silicide-infused porcelain ceramic 3D printing for dephosphorization and deoxygenation

Defect inhibition mechanism of 3D‐printed ceramics via synergetic resin composition and debinding processing regulation

Regulation of sintering procedure on property of DLP‐printing SiO2–Al2O3 ceramic: Key of cristobalite precipitation

POLYMER-DERIVED SIC CERAMIC WITH TRIPLY PERIOD MINIMAL SURFACE STRUCTURE FABRICATION THROUGH DIGITAL LIGHT PROCESSING

Impact of Sintering Aid Type and Content on the Mechanical Properties of Digital Light Processing 3D-Printed Si3N4 Ceramics

Effect of synergism of solid loading and sintering temperature on microstructural evolution and mechanical properties of 60 vol% high solid loading ceramic core obtained through stereolithography 3D printing

Sintering densification mechanism and mechanical properties of the 3D-printed high-melting-point-difference magnesium oxide/calcium phosphate composite bio-ceramic scaffold

Asynchronous Densification of Zirconia Ceramics Formed by Stereolithographic Additive Manufacturing

Study on Debinding and Sintering Processes for Ceramics Fabricated Using Digital Light Processing (DLP) 3D Printing

Optimizing the properties of vat photopolymerization 3D-printed SiC ceramics by multi-infiltration

Effect of silicon carbide additive on microstructure and properties of porcelain ceramics

The Mechanism of Porcelain Toughened by Activated Kaolinite in a Lower Sintering Temperature

Reducing Water Absorption and Improving Flexural Strength of Aluminosilicate Ceramics by MnO2 Doping

Investigation of the influence of process parameters on dimensional accuracy and post-sintering crack formation in ceramic 3D printing for porcelain-based commercial resins

Sintering Behavior and Technological Properties of Low-Temperature Porcelain Tiles Prepared Using a Lithium Ore and Silica Crucible Waste

Rheology and Printability of a Porcelain Clay Paste for DIW 3D Printing of Ceramics with Complex Geometric Structures

Infrared Irradiation to Drive Phosphate Condensation as a Route to Direct Additive Manufacturing of Oxide Ceramics

The influence of sintering procedure and porosity on the properties of 3D printed alumina ceramic cores

Influence of the Dispersants and Sintering Process on the Properties of Si2N2O Ceramics Via Digital Light Processing

Direct ink writing of aluminum-phosphate-bonded Al2O3 ceramic with ultra-low dimensional shrinkage

Preparation of Anorthite/Mullite In Situ and Phase Transformation in Porcelain