Elucidating influence of the existence formation of anchored cobalt phthalocyanine on electrocatalytic CO2-to-CO conversion
Shanhe Gong,Wenbo Wang,Xinxin Xiao,Jun Liu,Chundu Wu,Xiaomeng Lv
DOI: https://doi.org/10.1016/j.nanoen.2021.105904
IF: 17.6
2021-06-01
Nano Energy
Abstract:<p>Heterogeneous molecular catalysts with inexpensive transition-metal centers have attracted much attention, due to their excellent electrocatalytic performance on electrocatalytic carbon dioxide reduction reaction (CO<sub>2</sub>RR). Among them, metal phthalocyanine (MePc) has aroused great interest. However, the complex existence formation (crystals or evenly dispersion) in the hybrid catalyst, e.g. cobalt (II) phthalocyanine (CoPc), determining the final electrocatalytic CO<sub>2</sub>RR performance still remains debate. To further elucidate the influence of the existence formation of CoPc on electrocatalytic performance of CO<sub>2</sub>-to-CO conversion, we synthesized ultra-thin nitrogen-doped hollow carbon spheres (N-doped HCS) with a high surface area of 653.3 m<sup>2</sup> g<sup>−1</sup> as the support to anchor a series of different existence formation of CoPc. The existence formation of CoPc in the hybrid catalyst is closely related with the content of Co atom, the latter of which is the key factor of the CO<sub>2</sub>RR performance. We summarized the nonlinear relationship between the partial CO current density (<span class="math"><math>jCO</math></span>) and the content of Co atom at −0.82 V vs. RHE, and the equation of Faraday efficiency of CO (<span class="math"><math>FECO</math></span>) vs. the content of Co atom at −0.82 V vs. RHE, which proves the fact that the coexistence of crystals and evenly dispersed CoPc or evenly dispersed and low loading of CoPc both could reach the satisfying results (<span class="math"><math>jCO</math></span> > ~14 mA cm<sup>−2</sup>, <span class="math"><math>FECO</math></span> > ~ 91%, at −0.82 V vs. RHE) under the content of Co atom from 1.26 wt% to 0.14 wt%. The optimal catalyst (Co, 0.49 wt%) achieved a near-unity Faradaic efficiency of 96%, which is close to 4 times that of the unsupported CoPc (<span class="math"><math>FECO</math></span> =24.54%), and an outstanding current density of 20.47 mA cm<sup>−2</sup> towards CO, which is <em>c.a.</em> 60 times higher than that of the unsupported CoPc (0.34 mA cm<sup>−2</sup>) at −0.82 V vs. RHE. This work could potentially inspire the rational design of heterogeneous molecular catalysts and promote its application in the energy conversion and storage field.</p>
materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology