Bulk-like ZnSe Quantum Dots Enabling Efficient Ultranarrow Blue Light-Emitting Diodes
Min Gao,Huawei Yang,Huaibin Shen,Zaiping Zeng,Fengjia Fan,Beibei Tang,Jingjing Min,Ying Zhang,Qingzhao Hua,Lin Song Li,Botao Ji,Zuliang Du
DOI: https://doi.org/10.1021/acs.nanolett.1c02284
IF: 10.8
2021-08-24
Nano Letters
Abstract:Blue-emitting heavy-metal free QDs simultaneously exhibiting photoluminescence quantum yield close to unity and narrow emission line widths are essential for next-generation electroluminescence displays, yet their synthesis is highly challenging. Herein, we develop the synthesis of blue-emitting QDs by growing a thin shell of ZnS on ZnSe cores with their size larger than bulk Bohr diameter. The bulk-like size of ZnSe cores enables the emission to locate in the blue region with a narrow emission width close to its intrinsic peak width. The obtained bulk-like ZnSe/ZnS core/shell QDs display high quantum yield of 95% and extremely narrow emission width of ∼9.6 nm. Moreover, the bulk-like size of ZnSe cores reduces the energy level difference between QDs and adjacent layers in LEDs and improves charge transport. The LEDs fabricated with these high-quality QDs show bright pure blue emission with an external quantum efficiency of 12.2% and a relatively long operating lifetime.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.nanolett.1c02284.Synthesis and characteristics of QDs, QLED fabrication and characterization methods, steady-state PL spectra of different ZnSe core QDs measured at 298 and 77 K, molecule orbital plots of the highest occupied molecular orbital and lowest unoccupied molecular orbital states for different sizes of ZnSe QDs, PL QY of T-QDs and B-QDs, HRTEM image and EDS elemental mapping of T-QDs, XPS spectra, UPS spectra, single-dot PL spectra, and transient absorption (TA) spectra of QDs film, voltage-dependent EL spectra of QLEDs with T-QDs, CIE coordinates, and operational lifetimes of T-QDs- and B-QDs-based QLED (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology