One-step synthesis of Li2Mg2Mo3O12-(Li1/2Bi1/2)MoO4 composite ceramics with a stable temperature coefficient for ULTCC applications

Lifeng Ding,Ben Heng,Xia Feng,Wenjie Bian,Haikui Zhu,Lixi Wang,Yi Hou,Qitu Zhang

DOI: https://doi.org/10.1007/s10854-024-12647-9

2024-05-08

Journal of Materials Science Materials in Electronics

Abstract:Dielectric materials with near-zero τ f values are needed to enhance the thermal stability of devices and ensure their stability during temperatures changes. In this study, the introduction of the (Li 1/2 Bi 1/2 )MoO 4 phase was employed to regulate the τ f of the Li 2 Mg 2 Mo 3 O 12 system. A temperature-stable Li 2 Mg 2 Mo 3 O 12 -(Li 1/2 Bi 1/2 )MoO 4 composite ceramics were successfully synthesized using a one-step direct synthesis approach for the first time. The synthesis involved controlling the Li 2 CO 3 : MgO : Bi 2 O 3 : MoO 3 ratios at 1 : (2 − 1.5 x ) : x /2 : 3 ( x = 0.02 – 0.30). The impacts of different x values on phase composition, sintering properties and microwave dielectric properties were investigated. X-ray diffraction and Roman spectroscopy revealed the coexistence of the two phases without other miscellaneous phases. When x = 0.15, the excellent microwave dielectric properties were obtained with samples sintered at 600 °C for 2 h: ε r = 11.4, Q×f = 41,592 GHz ( f = 11.2 GHz), τ f = − 8 ppm/°C.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied