Novel BCZT-based ceramics with ultrahigh energy storage efficiency and outstanding high temperature fatigue endurance and stability for practical application

Zhemin Chen,Yongping Pu,Yating Ning,Chunhui Wu,Lei Zhang,Xuqing Zhang,Bo Wang

DOI: https://doi.org/10.1016/j.ceramint.2023.08.087

IF: 5.532

2023-08-01

Ceramics International

Abstract:Dielectric ceramic capacitors with superior energy storage efficiency and ability to operate in high temperature environments (T∼200 °C) are urgently needed for practical application. In this study, a relaxor component of Bi(Zn2/3Nb1/3)O3 (BZN) was massively doped into Ba0.85Ca0.15Zr0.1Ti0.9O3 (BCZT) ceramic to improve energy storage properties and ability to operate in high temperature. The massive introduction of Bi(Zn2/3Nb1/3)O3 optimizes dielectric relaxor behavior, enhances bandgap width, refines grain size and improves electrical homogeneity, which can significantly increase breakdown strength (E b), decrease remanent polarization (P r ) and broaden dielectric constant peak. Here, the 0.75BCZT-0.25BZN ceramic possesses an ultrahigh energy storage efficiency (∼96.8%) with a large recoverable energy density (∼2.39 J/cm3) under a medium applied field (260 kV/cm). In addition, the optimum sample exhibits prominent thermal stability within 20∼200°C and dielectric temperature stability (ΔC/C 25°C ≤ ± 15%, −63∼234°C) in accordance with X9R. More critically, the same composition was firstly measured fatigue endurance at 200°C and possesses excellent fatigue stability. The above results demonstrate that the optimum sample has potential for practical application in high temperature environments.

materials science, ceramics