Mechanical strength, biodegradation, and in vitro and in vivo biocompatibility of Zn biomaterials

Donghui Zhu, Irsalan Cockerill, Yingchao Su, Zhaoxiang Zhang, Jiayin Fu, Kee-Won Lee, Jun Ma, Chuka Okpokwasili, Liping Tang, Yufeng Zheng, Yi-Xian Qin, Yadong Wang

2019-01-29

Abstract:Zn-based biomaterials have emerged as promising new types of bioresorbable metallics applicable to orthopedic devices, cardiovascular stents, and other medical applications recently. Compared to other degradable metallic biomaterials (i.e., Mg- or Fe-based), Zn biomaterials have a more appropriate corrosion rate without hydrogen gas evolution. Here, we evaluated the potential of Zn-based metallics as medical implants, both in vitro and in vivo, alongside a standard benchmark Mg alloy, AZ31. The mechanical properties of the pure Zn were not strong enough but were significantly enhanced (microhardness > 70 kg/mm2, strength > 220 MPa, elongation > 15%) after alloying with Sr or Mg (1.5 at. %), surpassing the minimal design criteria for load-bearing device applications. The corrosion rate of Zn-based biomaterials was about 0.4 mm/year, significantly slower than that of AZ31. The measured cell viability and …