Abstract:Zinc (Zn) and some of its alloys are recognized as promising biodegradable implant materials due to their acceptable biocompatibility, facile processability, and moderate degradation rate. Nevertheless, the limited mechanical properties and stability of as-cast Zn alloys hinder their clinical application. In this work, hot-rolled (HR) and hot-extruded (HE) Zn-5 wt.% gadolinium (Zn-5Gd) samples were prepared by casting and respectively combining with hot rolling and hot extrusion for bone-implant applications. Their microstructure evolution, mechanical properties, corrosion behavior, cytotoxicity, antibacterial ability, and in vitro and in vivo osteogenesis were systematically evaluated. The HR and HE Zn-5Gd exhibited significantly improved mechanical properties compared with those of their pure Zn counterparts and the HR Zn-5Gd showed a unique combination of tensile properties with an ultimate tensile strength of ∼311.6 MPa, yield strength of ∼236.5 MPa, and elongation of ∼40.6%, all of which are greater than the mechanical properties required for bone-implant materials. The HR and HE Zn-5Gd showed higher corrosion resistance than their pure Zn counterpart in Hanks' solution and the HE Zn-5Gd had the lowest corrosion rate of 155 μm/y measured by electrochemical corrosion and degradation rate of 26.9 μm/y measured by immersion testing. The HR and HE Zn-5Gd showed high cytocompatibility toward MC3T3-E1 and MG-63 cells, high antibacterial effects against S. aureus , and better in vitro osteogenic activity than their pure Zn counterparts. Furthermore, the HE Zn-5Gd exhibited better in vivo biocompatibility, osteogenesis, and osteointegration ability than pure Zn and pure Ti. Statement of significance This work reports the mechanical properties, corrosion behaviors, cytocompatibility, antibacterial ability, in vitro and in vivo osteogenesis of biodegradable Zn–Gd alloy for bone-implant applications. Our findings demonstrate that the hot-rolled (HR) Zn–5Gd showed a unique combination of tensile properties with an ultimate tensile strength of ∼311.6 MPa, yield strength of ∼236.5 MPa, and elongation of ∼40.6%. The HR and HE Zn-5Gd showed higher corrosion resistance than their pure Zn counterpart in Hanks' solution. The HR and HE Zn-5Gd showed high cytocompatibility toward MC3T3-E1 and MG-63 cells, good antibacterial effects against S. aureus , and better in vitro osteogenic activity. Furthermore, the HE Zn-5Gd exhibited better in vivo biocompatibility, osteogenesis, and osteointegration ability than pure Zn and pure Ti.

Indirectly Extruded Biodegradable Zn-0.05wt%Mg Alloy with Improved Strength and Ductility: in Vitro and in Vivo Studies

<i>In vitro</i> and <i>in vivo</i> studies of Zn-Mn biodegradable metals designed for orthopedic applications

Research on Biodegradable Mg-Zn-Gd Alloys for Potential Orthopedic Implants: in Vitro and in Vivo Evaluations.

In Vitro and in Vivo Studies on As-Extruded Mg- 5.25Wt.%zn-0.6Wt.%ca Alloy As Biodegradable Metal

Design and characterizations of novel biodegradable Zn-Cu-Mg alloys for potential biodegradable implants

Microstructure, Mechanical Properties, in Vitro Degradation and Cytotoxicity Evaluations of Mg–1.5Y–1.2Zn–0.44Zr Alloys for Biodegradable Metallic Implants

Alloying design of biodegradable zinc as promising bone implants for load-bearing applications

Biodegradable Zn-Mn Alloys with Suitable Mechanical Strength, High Plasticity, and Good Osteogenic Activities for Orthopedic Applications

Biocompatibility of magnesium-zinc alloy in biodegradable orthopedic implants

A biodegradable Zn-5Gd alloy with biomechanical compatibility, cytocompatibility, antibacterial ability, and in vitro and in vivo osteogenesis for orthopedic applications

In Vivo Evaluation of Mg-5%Zn-2%Nd Alloy as an Innovative Biodegradable Implant Material

Nanoparticle-Enabled Zn-0.1Mg Alloy with Long-Term Stability, Refined Degradation, and Favorable Biocompatibility for Biodegradable Implant Devices

Evaluation of As‐extruded Ternary Zn–Mg–Zr Alloys for Biomedical Implantation Material: in Vitro and in Vivo Behavior

Micro-alloying with Mn in Zn–Mg alloy for future biodegradable metals application

Modulation of Osteogenesis and Angiogenesis Activities Based on Ionic Release from Zn–Mg Alloys

Endowing biodegradable Zinc implants with dual-function of antibacterial ability and osteogenic activity by micro-addition of Mg and Ag (≤ 0.1 wt.%)

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

Corrosion behavior, antibacterial properties and in vitro and in vivo biocompatibility of biodegradable Zn-5Cu-xMg alloy for bone-implant applications

Mechanical Strength, Biodegradation, and In Vitro and In Vivo Biocompatibility of Zn Biomaterials.

Microstructure, Mechanical Properties, and in Vitro Corrosion Behavior of Biodegradable Zn-1Fe-xMg Alloy

In Vitro Degradation Performance and Biological Response of a Mg–Zn–Zr Alloy