Performance of a rotating packed bed with blade packings in synthesizing nano-sized Fe 3 O 4 particles

Chia-Chang Lin,Yin-Ping Wu,Kuan-Yi Wu
DOI: https://doi.org/10.1016/j.jmrt.2023.09.272
IF: 6.267
2023-09-29
Journal of Materials Research and Technology
Abstract:Nano-sized Fe 3 O 4 particles were continuously synthesized in the rotating packed bed with blade packings where the rotational speed was set at 1800 rpm, the liquid flow rate of aqueous FeCl 2 /FeCl 3 was kept at 0.5 L/min, and the liquid flow rate of aqueous NaOH was maintained at 0.5 L/min with the chemical co-precipitation route that the synthesis temperature was fixed at 25°C, the FeCl 2 concentration was fixed at 0.15 mol/L, the FeCl 3 concentration was fixed at 0.3 mol/L, and the NaOH concentration was fixed at 1.2 mol/L. The average crystallite size and mean particle size of the as-synthesized nano-sized Fe 3 O 4 particles were 12.7 nm and 10.9 nm, respectively. The rate of continuous synthesis of nano-sized Fe 3 O 4 particles was 23.6 kg/day. The as-synthesized nano-sized Fe 3 O 4 particles exhibited a superparamagnetic characteristic at 25°C. Furthermore, the saturation magnetization of the as-synthesized nano-sized Fe 3 O 4 particles was 66.4 emu/g. The maximum Orange G adsorption capacity of the as-synthesized nano-sized Fe 3 O 4 particles at 25°C and pH 3 was 55.0 mg/g. This maximum Orange G adsorption capacity was much higher than that (5.7 mg/g) of the commercial nano-sized Fe 3 O 4 particles that were purchased from Sigma-Aldrich (SA-Fe 3 O 4 ) because the as-synthesized nano-sized Fe 3 O 4 particles had a smaller mean particle size. Accordingly, the as-synthesized nano-sized Fe 3 O 4 particles are a promising magnetic adsorbent in the removal of Orange G from water.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?