Depression of direct exchange couplings in metallic glasses: A comparative study of critical and electronic behavior in Gd6Co4.85 intermetallic compound and metallic glass

Guoming Cui,Xin Li,Guangcun Shan,Haibin Gao,Kam Wa Wong,Jiliang Zhang

DOI: https://doi.org/10.1016/j.intermet.2020.106878

IF: 4.075

2020-09-01

Intermetallics

Abstract:<p>Gd-based metallic glasses enable a wider exploration for excellent magnetocaloric materials due to no requirement of compositional stoichiometry, but these metallic glasses generally show a lower ordering temperature compared with corresponding intermetallic compounds. In this paper, critical behaviors for magnetic transitions in both Gd₆Co_4.85 intermetallic compound and metallic glass were carefully studied based on isothermal magnetization to reveal the exchange interactions in these two different structural stages, together with experimental electronic density analyses on the compound. Obtained critical exponents close to the theoretical values predicted by the mean-field theory (MFT) in both structures suggest the majority of Gd–Gd long-range exchange interactions, while the Co-Co direct interaction accounts for the deviation of these exponents from the theoretical values in MFT. This is likely a common feature for rare earth – transition metal ferrimagnets. The ordered Co atoms in the intermetallic compound exhibit a high-spin state (~4.6 <em>μ</em>_<em>B</em>), in contrast with the low-spin state of Co (~1.2 <em>μ</em>_<em>B</em>) in the metallic glass. The reduced spin is associated with the liquid-like structure in the metallic glass (e.g. longer Co-Co distances) and responsible for the low ordering temperature. This work also indicates that the substitution of p-block elements like Al prefers the site to diminish Co moments, leading to the significantly reduced ordering temperature, and thus emphasizes the critical role of <em>d</em>-electron elements to maintain enough direct exchange interactions for proper transition temperature in the development of new metallic glasses with giant magnetocaloric effects.</p>

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the key behaviors of magnetic transitions in Gd6Co4.85 intermetallic compounds and amorphous alloys, as well as the exchange interactions in these different structural phases. Specifically, the research aims to carefully study the key behaviors of Gd6Co4.85 intermetallic compounds and amorphous alloys during magnetic transitions through isothermal magnetization, and at the same time, combine experimental electron density analysis to reveal the exchange interaction mechanisms in these two materials. The study found that the key exponents of the two structures are close to the theoretical values predicted by the mean - field theory (MFT), indicating that the Gd - Gd long - range exchange interaction is dominant, while the Co - Co direct interaction leads to the deviation of these exponents from the MFT theoretical values. In addition, the study also pointed out that the doping of p - block elements such as aluminum tends to reduce the Co moment, thereby significantly reducing the ordering temperature, emphasizing the importance of d - electron elements in maintaining sufficient direct exchange interaction to achieve an appropriate transition temperature, which is crucial for the development of new amorphous alloys with a large magnetocaloric effect.