The Performance of Niobium-Microalloying Ultra-High-Strength Bridge Cable Steel during Hot Rolling

Jie Zhou,Zhichao Yu,Jiahui Chen,Sheng Wu,Kaiming Wu,Libo Pan

DOI: https://doi.org/10.3390/ma17061259

IF: 3.4

2024-03-09

Materials

Abstract:This study focuses on exploring the effects of niobium (Nb)-microalloying on the properties of steel for ultra-high-strength bridge cables during hot-rolling processes. We employed a combination of dual-pass compression tests, stress–strain curve analysis, and Electron Backscatter Diffraction (EBSD) techniques to investigate the influence of Nb-microalloying on the static recrystallization behavior and grain size of the steel. The key findings reveal that Nb-microalloying effectively inhibits static recrystallization, particularly at higher temperatures, significantly reducing the volume fraction of recrystallized grains, resulting in a finer grain size and enhanced deformation resistance. Secondly, at a deformation temperature of 975 °C, Nb-containing steel exhibited finer grain sizes compared to Nb-free steel when held for 10 to 50 s; however, the grain size growth accelerated when the hold time exceeded 50 s, likely linked to the increased deformation resistance induced by Nb. Lastly, this research proposes optimal hot-rolling process parameters for new bridge cable steel, recommending specific finishing rolling temperatures and inter-pass times for both Nb-containing and Nb-free steels during the roughing and finishing stages. This study suggests optimal hot-rolling parameters for both Nb-containing and Nb-free steels, providing essential insights for improving hot-rolling and microalloying processes in high-carbon steels for bridge cables.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

### Problems Addressed by the Paper

This paper primarily investigates the impact of niobium (Nb) microalloying on the performance of ultra-high-strength bridge cable steel during the hot rolling process. Specifically, the study delves into the effects of Nb microalloying on the static recrystallization behavior and grain size of the steel through double-pass compression experiments, stress-strain curve analysis, and Electron Backscatter Diffraction (EBSD) techniques.

**Key findings include:**
1. **Inhibition of Static Recrystallization**: Nb microalloying effectively inhibits static recrystallization at high temperatures, significantly reducing the volume fraction of recrystallized grains, leading to finer grain sizes and higher deformation resistance.
2. **Grain Size Variation**: When deformed at 975°C, Nb-containing steel exhibits finer grain sizes within a holding time of 10 to 50 seconds; however, when the holding time exceeds 50 seconds, grain size growth accelerates, which may be related to the increased deformation resistance caused by Nb.
3. **Optimization of Hot Rolling Process Parameters**: The study proposes optimal hot rolling process parameters for new bridge cable steel, recommending specific finishing rolling temperatures and inter-pass times for Nb-containing and Nb-free steels during roughing and finishing stages. This provides important insights for improving the hot rolling and microalloying processes of high-carbon bridge cable steel.

In summary, this paper aims to explore the effects of Nb microalloying on the performance of 2000 MPa-grade ultra-high-strength bridge cable steel during the hot rolling process and proposes optimized hot rolling process parameters.