Cold sintered, temperature-stable CaSnSiO5-K2MoO4 composite microwave ceramics and its prototype microstrip patch antenna

Yuping Ji,Kaixin Song,Shiyu Zhang,Zhilun Lu,Ge Wang,Linhao Li,Di Zhou,Dawei Wang,Ian M. Reaney
DOI: https://doi.org/10.1016/j.jeurceramsoc.2020.08.053
IF: 5.7
2021-01-01
Journal of the European Ceramic Society
Abstract:Dense (1-x)wt%CaSnSiO5-xwt%K2MoO4 (CSSO-KMO) composite ceramics were fabricated by the cold sintering process at 180 °C under 400 MPa for 60 min. X-ray diffraction, Energy dispersive X-ray and Raman spectroscopy confirmed that CSSO and KMO coexisted without intermediate phases. As KMO weight fraction increased, relative permittivity (ε r) and temperature coefficient of resonant frequency (τf ) decreased and the microwave quality factor (Q×f, where f is resonant frequency) increased. Near-zero τf (-0.5 ppm/°C) was obtained for 65 wt%CSSO-35 wt%KMO with ε r ∼ 9.2 and Q×f ∼ 6240 GHz. No chemical reaction between ceramic composites and silver was observed, demonstrating potential for cofiring with Ag-paste. A prototype antenna was fabricated from 65 wt%CSSO-35 wt%KMO composite ceramic with a bandwidth of 144 MHz @ -10 dB, a gain of 5.7 dBi and a total efficiency of 88.4 % at 5.2 GHz, suitable for 5 G mobile communication systems.
materials science, ceramics
What problem does this paper attempt to address?