Abstract:Microwave dielectric ceramics are vital for filters, dielectric resonators, and dielectric antennas in the 5G era. It was found that the (Cu1/3Nb2/3)4+ substitution can effectively adjust the TCF (temperature coefficient of resonant frequency) of Li2TiO3 and simultaneously increase its Q × f (Q and f denote the quality factor and the resonant frequency, respectively) value. Notably, excellent microwave dielectric properties (εr (permittivity) ≈ 18.3, Q × f ≈ 77,840 GHz, and TCF ≈ +9.8 ppm/°C) were achieved in the Li2Ti0.8(Cu1/3Nb2/3)0.2O3 (LTCN0.2) ceramic sintered at 1140 °C. Additionally, the sintering temperature of LTCN0.2 was reduced to 860 °C by the addition of 3 wt % H3BO3, exhibiting superior microwave dielectric properties (εr ≈ 21.0, Q × f ≈ 51,940 GHz, and TCF ≈ 1.4 ppm/°C) and being chemically compatible with silver. Moreover, LTCN0.2 + 3 wt % H3BO3 ceramics were designed as a patch antenna and a dielectric resonator antenna, both of which showed high simulated radiation efficiencies (88.4 and 93%) and gains (4.1 and 4.03 dBi) at the center frequencies (2.49 and 10.19 GHz). The LTCN0.2 + 3 wt % H3BO3 materials have promising future application for either 5G mobile communication devices and/or in low-temperature co-fired ceramic technology owing to their high Q, low sintering temperature, small density, and good temperature stability.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c18836?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c18836</a>.Refined lattice parameters of LTCNx (0 ≤ x ≤ 0.4) ceramics (Table S1), Raman spectra of LTCNx (0 ≤ x ≤ 0.4) ceramics (Figure S1), SEM images and densities of the LTCNx (0 ≤ x ≤ 0.4) specimens (Figure S2), phonon parameters achieved from the fitting of the infrared reflectivity spectra of the LTCN0.2 specimen (Table S2), phonon parameters achieved from the fitting of the infrared reflectivity spectra of the LTCN0.2 + 3 wt % H3BO3 ceramic (Table S3), and optimized parameters of the proposed patch antenna (Table S4) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c18836/suppl_file/am0c18836_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Design and Fabrication of a Satellite Communication Dielectric Resonator Antenna with Novel Low Loss and Temperature-Stabilized (Sm 1– x Ca x ) (Nb 1– x Mo x )O 4 ( x = 0.15–0.7) Microwave Ceramics

Design of a Sub-6 GHz Dielectric Resonator Antenna with Novel Temperature-Stabilized (Sm1-Xbix)nbo4 (X=0-0.15) Microwave Dielectric Ceramics

Design of a Sub-6 GHz Dielectric Resonator Antenna with Novel Temperature-Stabilized (Sm 1– x Bi x )NbO 4 ( x = 0–0.15) Microwave Dielectric Ceramics

Temperature-Stable x (Na 0.5 Bi 0.5 )MoO 4 –(1– x )MoO 3 Composite Ceramics with Ultralow Sintering Temperatures and Low Dielectric Loss for Dielectric Resonator Antenna Applications

Structure-property relationships of novel microwave dielectric ceramics with low sintering temperatures: (Na(0.5x)Bi(0.5x)Ca(1-x))MoO(4).

Novel scheelite‐type [Ca 0.55 (Nd 1‐ x Bi x ) 0.3 ]MoO 4 (0.2 ≤ x ≤ 0.95) microwave dielectric ceramics with low sintering temperature

Microwave Dielectric Properties and Vibrational Spectra of (na0.5xla1–0.5x)(nb1−xmox)o4 Ceramics with Scheelite Structures

Nonstoichiometric microwave dielectric ceramics [(Na0.5-xBi0.5+x/3)0.5Ca0.5]MoO4 with low sintering temperatures

Novel Scheelite‐type [ca0.55(nd1‐xbix)0.3]moo4 (0.2 ≤ X ≤ 0.95) Microwave Dielectric Ceramics with Low Sintering Temperature

Design and Fabrication of a C-Band Dielectric Resonator Antenna with Novel Temperature-Stable Ce(Nb 1- x V x )NbO 4 ( x = 0-0.4) Microwave Ceramics

Temperature independent low firing [Ca0.25(Nd1-xBix)0.5]MoO4 (0.2 ≤ x ≤ 0.8) microwave dielectric ceramics

Temperature Stable Sm(Nb1−xVx)O4 (0.0 ≤ X ≤ 0.9) Microwave Dielectric Ceramics with Ultra-Low Dielectric Loss for Dielectric Resonator Antenna Applications

Crystal structure and microwave dielectric properties of A- and B-site co-substituted NdNbO 4 ceramics

Microwave Dielectric Properties of Low Firing Temperature Stable Scheelite Structured (Ca,bi)(mo,v)o-4 Solid Solution Ceramics for LTCC Applications

Structure, spectral analysis and microwave dielectric properties of novel x(NaBi)0.5MoO4-(1-x)Bi2/3MoO4 (x = 0.2 ∼ 0.8) ceramics with low sintering temperatures

Design of a High-Efficiency and -Gain Antenna Using Novel Low-Loss, Temperature-Stable Li 2 Ti 1 – x (Cu 1/3 Nb 2/3 ) x O 3 Microwave Dielectric Ceramics

Influence of W substitution on crystal structure, phase evolution and microwave dielectric properties of (Na0.5Bi0.5)MoO4 ceramics with low sintering temperature

Crystal structure, chemical bond characteristics, infrared reflection spectrum, and microwave dielectric properties of Nd-2(Zr(1-x)Tix)(3)(MoO4)(9) ceramics

Coordinated Modification Of Microstructures And Properties In Ba6-3xnd8+2xti18o54 Microwave Dielectric Ceramics

Temperature stable Sm(Nb 1−x V x )O 4 (0.0 ≤ x ≤ 0.9) microwave dielectric ceramics with ultra-low dielectric loss for dielectric resonator antenna applications

Novel temperature stable (Na0.5Y0.5)MoO4 microwave dielectric ceramics with TiO2 addition