Abstract:Polymers are frequently considered as a candidate material for heavy duty tribological applications. Standard tribological testing for such applications may result in unrealistic tribological properties in terms of wear mechanism, transfer film formation and friction coefficient etc. Thus the present research aims to explore the tribological behaviour of currently available neat polymers under heavy duty loading condition. In this background, nine different polymers (PAI, PEI, PC, PPSU, PA6, PET, PPS, PVDF, and UHMWPE) of amorphous and semi-crystalline groups were chosen from engineering and high performance grades. Large scale reciprocating sliding wear tests with 50×50mm contact area were used. Considering heavy duty loading condition, the operational parameter were idealised at 10kN normal force and 50mm/s sliding speed. From the test results the polymers are classified into three groups based on the wear mechanisms and the transfer layer characteristics observed from the counterface. Group 1 did not persist any transfer layer (PC and PEI), whereas Group 2 materials (PET, PPS, PPSU and PAI) has lumpy discontinuous transfer layer and finally Group 3 materials evidenced uniform thin transfer layer. Clear signs of three body abrasion were evidenced in Group 1 material which is due to the absence of transfer layer and also from the large loose debris. Poor adhesion of inhomogeneous lumpy transfer layer in Group 2 showed an intermediate wear rate. Based on the wear and friction performance, the Group 3 materials (PVDF, UHMWPE and PA6) are proposed as the candidate materials for heavy duty tribological application. In regards to the transfer layer thickness and wear mechanisms at large scale testing, the present observations showed incomparable results with the literature. This research concludes that the revisit to polymer tribology at high load condition has indicated the difference in wear mechanism and the corresponding tribological characteristics in large scale testing. As a future work multi-scale testing is an absolute must for the complete understanding of tribological characteristics w.r.t a specific material.

Abrasive wear of some commercial polymers

Abrasive wear behaviour of polymeric materials

An investigation of the wear of polymeric materials

Large-scale tests on friction and wear of engineering polymers for material selection in highly loaded sliding systems

Abrasive wear of graphite fiber-reinforced polymer composite materials

Friction and wear performance of polyether ether ketone (PEEK) polymers in three lubrication regimes

Abrasive Sensitivity of Engineering Polymers and a Bio-Composite under Different Abrasive Conditions

Characteristics and mechanism of abrasive wear for thermoplastic polymers

Influence of fillers and fibre reinforcement on abrasive wear resistance of some polymeric composites

Friction and wear properties of polymer, metal, and ceramic prosthetic joint materials evaluated on a multichannel screening device

Comparative Evaluation of the Tribological Properties of Polymer Materials with Similar Shore Hardness Working in Metal–Polymer Friction Systems

Revisiting polymer tribology for heavy duty application

Abrasive wear of PEEK and ATSP-based polymer composite coatings under lunar regolith conditions

On the ability of polymers to self-lubrication in metal – polymer friction pairs

Evaluation of polymer composites for sliding and abrasive wear applications

Comparative Evaluation of Tribological Effectiveness of Carbon- and Glass-Filled Polyamide Composites Using Submicromechanical Diagnostics of Surface Layers before and after Wear Tests during Dry Sliding Friction

Tribological performance of polymer composites used in electrical engineering applications

The influence of polymer composition on the wear of the metal surface during fretting of steel on polymer

Influence of Load and Sliding Velocity on Abrasive Wear of Polyester Composites Reinforced with Bio-Particulates as Filler Material

Wear performance of bulk oriented nanocomposites UHMWPE/FMWCNT and metal-polymer composite sliding bearings

Mechanical and Tribological Performances of Thermoplastic Polymers Reinforced with Glass Fibres at Variable Fibre Volume Fractions