Lewis metal salt synthesis of V 2 C (MXene) composite nickel diselenide as a high-performance cathode material for secondary aluminum batteries

Yi Wang,Wenrong Lv,Gaohong Wu,Wenming Zhang,Zhanyu Li

DOI: https://doi.org/10.1016/j.apsusc.2023.157911

IF: 6.7

2023-06-29

Applied Surface Science

Abstract:Rechargeable aluminum batteries are promising energy storage devices that have advantages over lithium-ion batteries in terms of safety, cost, and capacity. Herein, a V 2 C (MXene) composite nickel diselenide (V 2 2 ) cathode is synthesized by etching V 2 AlC MAX phase via Lewis acidic molten salts and then calcining it with selenium. The V 2 2 cathode material exhibited reversible redox reactions of Ni 2+ /Ni x+ , and Se - /Se x+ in the charge-discharge process. Due to the fact that selenium can also replace functional groups on V 2 C, it can effectively avoid strong interactions between AlCl 4 - and V 2 C layers, thereby increasing their energy density. By using V 2 2 as the cathode material for aluminum batteries, the first cycle discharge specific capacity reached 486.8 mAh g -1 and remained at 166 mAh g -1 after about 3800 cycles at 1 A g -1 . To compare the performance of the V 2 2 cathode material, additional cathode materials (V 2 , V 2 , V 2 2 , and V 2 ) are created using a similar synthesis process. This work demonstrates a novel synthesis method of intercalation-type composite low-dimensional cathode materials for stable secondary aluminum batteries.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films