Abstract:A cement paste or mortar is composed of a mineral skeleton with micron to millimeter-sized grains, surrounded by water filaments. The cohesion or shear resistance in the cement paste and mortar is caused by capillary forces of action. In the case of mortar mixes, there is friction between the particles. Therefore, the mortar mixture shows both friction between particles and cohesion, while the paste shows only cohesion, and the friction between particles is negligible. The property of the cement paste is greatly influenced by the rheological characteristics like cohesion and internal angle friction. It is also interesting that when studying the rheology of fresh concrete, the rheological behavior of cement paste and mortar has direct applicability. In this paper, the rheological characteristics of cement paste and mortar with and without mineral admixtures, that is, fly ash and ground granulated blast-furnace slag (GGBS), were studied. A cement mortar mix with a cement-to-sand ratio of 1:3 was investigated, including fly ash replacement from 10% to 40%, and GGBS from 10% to 70% of the weight of the cement. A suitable blend of fly ash, GGBS, and ordinary Portland cement (OPC) was also selected to determine rheological parameters. For mortar mixtures, the flow table was conducted for workability studies. The flexural and split tensile strength tests were conducted on various mortar mixtures for different curing times. The results indicate that in the presence of a mineral mixture of fly ash and GGBS, the rheological behavior of paste and mortar is similar. Compared with OPC-GGBS-based mixtures, both cement with fly ash and ternary mixtures show less shear resistance or impact resistance. The rheological behavior of the mortar also matches the rheological behavior in the flow table test. Therefore, it is easy to use the vane shear test equipment to conduct cohesion studies to understand the properties of cement paste and mortar using mineral admixtures. The strength results show that the long-term strength of GGBS-based mixtures and ternary mixed mixtures is better than that of fly-ash-based mixtures. For all mixtures, the strength characteristics are greatest at a w/b ratio of 0.6.

Effect of Fly Ash Content on Rheological Properties of Self-compacting Geopolymer Mortar

Mix Design Processing for Self Compacting Geopolymer Mortar

Effect of Additives on the Rheological and Mechanical Properties of Microfine-Cement-Based Grout

Effect of Fine Aggregate Particle Characteristics on Mechanical Properties of Fly Ash-Based Geopolymer Mortar

Experimental study on full-volume fly ash geopolymer mortars: Sintered fly ash versus sand as fine aggregates

Effect of water‐reducing admixtures water content on rheology, workability, and mechanical properties of fly ash‐based geopolymer and slag‐based alkali‐activated mixtures

Study on the Effect of Recycled Fine Aggregate Qualities on Fly Ash/GGBS-Based Geopolymer Mortar

An Enhanced Mix Design Method of Self-Compacting Concrete with Fly Ash Content Based on Paste Rheological Threshold Theory and Material Packing Characteristics

The Role of Rice Husk Ash in Enhancing the Fresh Properties, Density, and Compressive Strength of Fly Ash Based Self Compacting Geopolymer Concrete

Effects of Sand/Fly Ash and the Water/Solid Ratio on the Mechanical Properties of Engineered Geopolymer Composite and Mix Design Optimization

Workability and Compressive Strength Properties of (Fly Ash-Metakaolin) based Flowable Geopolymer Mortar

Experimental study on performances of fly ash-based geopolymer cementitious material with low admixtures content

Rheological Behavior and Strength Characteristics of Cement Paste and Mortar with Fly Ash and GGBS Admixtures

Using Municipal Solid-Waste Incinerator Fly Ash, Wash Water, and Propylene Fibers in Self-Compacting Repair Mortar, Greenhouse Gas Emissions Potential

Sustainable use of silica fume and metakaolin in slag/fly ash-based self-compacting geopolymer composites: Fresh, physico-mechanical and durability properties

Effects of Relative Humidity on the Properties of Fly Ash-Based Geopolymers

Influence Mechanisms of Fly Ash in Magnesium Ammonium Phosphate Cement

Expansion in low calcium fly ash-based geopolymer concrete: chemical factors influenced by silica fume and NaOH concentration

Utilization of Fly Ash as a Viscosity-Modifying Agent to Produce Cost-Effective, Self-Compacting Concrete: A Sustainable Solution

Effect of Mineral Admixtures on Physical, Mechanical, and Microstructural Properties of Flue Gas Desulfurization Gypsum-Based Self-Leveling Mortar

Mechanical Properties, Permeability and Microstructure of Steam-Cured Fly Ash Mortar Mixed with Phosphogypsum