Mixed phase sodium manganese oxide as cathode for enhanced aqueous zinc-ion storage

Xinyu Wang,Xinghua Qin,Qiongqiong Lu,Mingming Han,Ahmad Omar,Daria Mikhailova

DOI: https://doi.org/10.1016/j.cjche.2020.05.015

IF: 3.8

2020-08-01

Chinese Journal of Chemical Engineering

Abstract:Aqueous zinc-ion batteries have been regarded as a promising alternative to large-scale energy storage, due to associated low-cost, improved safety and environmental friendliness. However, a high-performance cathode material for both rate capability and specific capacity is still a challenge. One kind of the more promising candidates are sodium manganese oxide (NMO) materials, although they suffer from individual issues and need to be further improved. Herein, we present a novel mixed phase NMO material composed of nearly equal amounts of Na_0.55Mn₂O₄ and Na_0.7MnO_2.05. The structured configuration with particle size of 200-500 nm is found to be beneficial towards improving the ion diffusion rate during the charge/discharge process. Compared with Na_0.7MnO_2.05 and Na_0.55Mn₂O₄, the mixed phase NMO demonstrates an enhanced rate capability and excellent long-term cycling stability with a capacity retention of 83% after 800 cycles. More importantly, the system also delivers an impressive energy density and power density, as 378 Wh kg^-1 at 68.7 W kg^-1, or 172 Wh kg^-1 at 1705 W kg^-1. The superior electrochemical performance is ascribed to the fast Zn²⁺ diffusion rate because of a large ratio of capacitive contribution (63.9% at 0.9 mV s^-1). Thus, the mixed phase route provides a novel strategy to enhance electrochemical performance, enabling mixed phase NMO as very promising material towards large-scale energy-storage applications.

engineering, chemical