Abstract:The uncoated γ‐Ce2S3 is easy to decompose and release toxic gas H2S in a humid or acidic environment, and its air thermal stability is limited to 350°C. In this work, we have used heterogeneous precipitation method to coat the surface of γ‐Ce2S3 powder with ZnO nano‐layer, and then used microemulsion method to coat the surface of γ‐Ce2S3@ZnO with SiO2, and successfully prepared γ‐Ce2S3@ZnO@SiO2 composite coating powder. On the premise of not affecting the color rendering performance as much as possible, the thermal stability of γ‐Ce2S3 powder is improved from 350 to 514°C, the time stability is improved from less than 40 days to more than 360 days, and the acid corrosion stability and safety performance are significantly improved. As an environment‐friendly powder with good coloring performance, rare earth sulfide is one kind of the important choices to replace cadmium and lead colorants. In particular, γ‐Ce2S3 belongs to rare earth sesquisulfide, which has a bright red color. However, the uncoated γ‐Ce2S3 is easy to decompose and release H2S in a humid or acidic environment, and its air thermal stability is limited to 350°C. In this work, γ‐Ce2S3 powders coated with zinc oxide were prepared by heterogeneous precipitation method, and a dense protective layer was formed by ZnO to improve chemical and thermal stability. Moreover, silicon dioxide was deposited on the surface of the zinc oxide coating using the microemulsion process to strengthen the powder's acid resistance. The double shells structure greatly promoted thermal stability and acid resistance of γ‐Ce2S3 powders. The results showed that rare earth sulfide powders with double shells have good stability for coloring applications.

Impurity doping effects and ecological friendly synthesis of cerium sulfide powders for enhanced chromaticity and color tunability

Promoting thermal stability and acid resistance of rare earth sulfide powders by coating ZnO and SiO2 double shells

Modulating interfacial defects for dual-enhancing chromaticity and stability of cerium sulfide

Dual-enhancement of chromaticity and thermal stability: In-situ synthesis of core–shell γ-Ce2S3@CePO4 configuration

Synthesis of Ce–Ni/sepiolite with Excellent Adsorption and Catalytic Oxidation Performance Toward Dyes

Synthesis and characterization of (Pr, Ce)‐ZrSiO 4 ceramic pigments: The properties of the pigments and the effect of Ce

Advancements in Synthesis and Application of Rare Earth Sulfides

Selenization of Cu2ZnSnS4 Enhanced the Performance of Dye-Sensitized Solar Cells: Improved Zinc-Site Catalytic Activity for I-3(-)

Synergistic Co/S co-doped CeO 2 sulfur-oxide catalyst for efficient catalytic reduction of toxic organics and heavy metal pollutants under dark conditions

Synthesis and photocatalytic properties of Cerium(IV) oxide graphene oxide composites

Novel Cerium‐Based Sulfide Nano‐Photocatalyst for Highly Efficient CO2Reduction

Facile synthesis of Ce(III)-rich cerium oxyhydroxide and its unselective adsorption of Sb(III) and Sb(V) via oxygen vacancies

Preparation and Characterization of Fine Sr2ceo4 Blue Phosphor Powders

The Effect of Doping Sr~(2+) on Enhancement of Red Emission of Y_(2.78-x)Sr_xGd_(0.1)Al_5O_(12)∶0.06Ce~(3+) Phosphors

Red, green and blue emissions coexistence in white-light-emitting Ca 11(SiO4)4(BO3)2:Ce 3+,Eu2+,Eu3+ phosphor

Preparation of Ternary Rare Earth Sulfide LaxCe2–xS3 As Red Pigment

Rapid synthesis and mechanochemical reactions of cesium copper halides for convenient chromaticity tuning and efficient white light emission

PREPARATION AND CHARACTERIZATION OF TiO2/SERICITE COMPOSITE MATERIAL WITH FAVORABLE PIGMENTS PROPERTIES

Nitrogen and sulfur co-doping CeO2 nanorods for efficient photocatalytic VOCs degradation

Ecofriendly High NIR Reflectance Ceramic Pigments Based on Rare Earths Compared with Classical Chromophores Prepared by DPC Method

Facile one-pot synthesis of carbon self-doped graphitic carbon nitride loaded with ultra-low ceric dioxide for high-efficiency environmental photocatalysis: Organic pollutants degradation and hexavalent chromium reduction