Abstract:Magnesium (Mg) alloys containing rare earths (RE) gained special attention as promising candidates for degradable implant applications. Cerium (Ce) is one of the RE elements which can be tolerated by the human physiological system when used as an alloying element in Mg alloys. In this current research work, Mg-Ce binary alloys (0%, 0.5%, 1%, 1.5%, and 2% Ce by weight) were prepared by the stir-casting method. The developed alloys were characterised, and corrosion performance was assessed by immersion experiments in normal saline solution and by electrochemical experiments. The degradation rate of the developed alloys was measured as decreased with the increased Ce content up to 1.5%. From the polarisation studies, lower corrosion current density values 3.5 × 10 −5 A/cm 2 and 4.1 × 10 −5 A/cm 2 were observed for Mg-1.5%Ce and Mg-2%Ce alloys, respectively compared with the other samples. The surface morphologies after removing the corrosion products revealed more degraded regions for Mg and alloys with lower Ce content (0.5% and 1%) compared with 1.5% and 2% Ce. From the results, it is concluded that developing an Mg-Ce alloy with an optimum fraction of Ce (1.5%) is promising to produce degradable Mg-based medical implants with controlled degradation. Récemment, les alliages de magnésium (Mg) contenant des terres rares (TR) ont retenu une attention particulière en tant que candidats prometteurs pour les applications d'implants dégradables. Le cérium (Ce) est l'un des éléments de TR qui peuvent être tolérés par le système physiologique humain lorsqu'il est utilisé comme élément d'alliage dans les alliages de Mg. Dans ces travaux de recherche en cours, on a préparé des alliages binaires Mg-Ce (0%, 0.5%, 1%, 1.5% et 2% Ce en poids) par la méthode de coulée avec agitation. On a caractérisé les alliages développés et l'on a évalué leurs performances à la corrosion par des expériences d'immersion dans une solution saline normale et par des expériences électrochimiques. On a mesuré la vitesse de dégradation des alliages développés comme diminuant avec l'augmentation de la teneur en Ce jusqu'à 1.5%. À partir des études de polarisation, on a observé des valeurs de densité de courant de corrosion plus faibles de 3.5 × 10 −5 A/cm 2 et de 4.1 × 10 −5 A/cm 2 pour les alliages Mg-1.5%Ce et Mg-2%Ce, respectivement, par rapport aux autres échantillons. Les morphologies de surface après l'élimination des produits de corrosion ont révélé des régions plus dégradées pour le Mg et pour les alliages à plus petite teneur en Ce (0.5% et 1%) contre 1.5% et 2% de Ce. À partir de ces résultats, il est conclu que le développement de l'alliage Mg-Ce avec une fraction optimale de Ce (1.5%) promet de produire des implants médicaux dégradables à base de Mg avec une dégradation contrôlée.

Effect of the addition of low rare earth elements (lanthanum, neodymium, cerium) on the biodegradation and biocompatibility of magnesium

Research progress on corrosion behaviors and biocompatibility of rare-earth magnesium alloys in vivo and in vitro

Effects of Different Rare Earth Elements on the Degradation and Mechanical Properties of the ECAP Extruded Mg Alloys

A review of the physiological impact of rare earth elements and their uses in biomedical Mg alloys

Design of single-phased magnesium alloys with typically high solubility rare earth elements for biomedical applications: Concept and proof

Development of Magnesium-Based Biodegradable Metals with Dietary Trace Element Germanium As Orthopaedic Implant Applications.

Biomedical rare-earth magnesium alloy: Current status and future prospects

Degradable magnesium-based alloys for biomedical applications: The role of critical alloying elements

Biocompatibility of bioabsorbable Mg–Ca alloys with rare earth elements addition

Significance of Alloying Elements on the Mechanical Characteristics of Mg-Based Materials for Biomedical Applications

Zinc and cerium synergistically enhance the mechanical properties, corrosion resistance, and osteogenic activity of magnesium as resorbable biomaterials

Effect of rare earth elements Ce and Yb on the in vitro properties of biodegradable Zn alloys

Effects of extract solution from magnesium alloys supplemented with different compositions of rare earth elements on in vitro epithelial and osteoblast progenitor cells

In Vitro and in Vivo Studies on Biomedical Magnesium Low-Alloying with Elements Gadolinium and Zinc for Orthopedic Implant Applications

Corrosion and biocompatibility improvement of magnesium-based alloys as bone implant materials: a review

Development of rare-earth oxide reinforced magnesium nanocomposites for orthopaedic applications: A mechanical/immersion/biocompatibility perspective

In vivo performance of a rare earth free Mg-Zn-Ca alloy manufactured using twin roll casting for potential applications in the cranial and maxillofacial fixation devices

Corrosion behaviour of the magnesium-cerium binary alloy designed for degradable medical implants

Enhanced antimicrobial properties, cytocompatibility, and corrosion resistance of plasma-modified biodegradable magnesium alloys

Recent advances on the development of magnesium alloys for biodegradable implants

Impact of scandium and terbium on the mechanical properties, corrosion behavior, and biocompatibility of biodegradable Mg-Zn-Zr-Mn alloys