Abstract:Two novel bismaleimide (BMI) monomers containing 1,3,4-oxadiazole, i.e., 5-tert-butyl-1,3-di[5-(4-maleimidophenyl)-1,3,4-oxadiazole-2-yl]benzene (Buoxd) and 4,4′-[5-(4-maleimidophenyl)-1,3,4-oxadiazole-2-yl]diphenyldimethylsilane (Sioxd), were designed, synthesized and copolymerized with 4,4′-bismaleimidodiphenylmethane (BMDM) to yield a new series of high-performance bismaleimide resins. Both monomers obtained are readily soluble in common organic solvents, such as dichloromethane and chloroform, enabling an easy solution processing. The thermal properties of the two monomers were carefully studied by the differential scanning calorimetry (DSC), optical microscopy and thermogravimetric analysis (TGA, simultaneous DSC). The BMI resins based on a mixture of Buoxd (or Sioxd) and BMDM in a weight ratio of 10% were prepared. DSC investigations showed that the thermal curing of the BMI resins could be accomplished at a lower temperature than the thermal curing temperatures of Buoxd and Sioxd, and the thermal processing window, i.e., the temperature range between the melting transition and thermal curing process, was over 26°C. The thermal properties and thermal mechanical properties of the resulting BMI resins were investigated by DSC, thermogravimetric analysis (TGA) and dynamic mechanical analysis (DMA). No glass transition temperature was found in the range of 50–350°C, and very good thermal stability (Td>490°C in nitrogen) and high thermo-oxidative stability (Td>460°C in air) were revealed. Composites composed of the above BMI resins and glass cloth were also prepared, which showed high bending modulus (>1.6GPa) at a very high temperature (e.g., 400°C).

Synthesis, polymerization kinetics, and thermal properties of novel bismaleimides containing twisted structure

Curing, Thermal Stability and Composite Properties for Blends of the Novel Bismaleimide and Cyanate Containing Naphthalene

Study on Curing Kinetics and Thermal Properties of Bismaleimide Resin Containing Ether Linkage

Novel Full Bio-Based Phloroglucinol Benzoxazine Resin: Synthesis, Curing Reaction and Thermal Stability

Synthesis and Cure of Liquid Crystalline Diallyl Modifiers for Bismaleimide Resin

Synthesis of Aromatic Diamine-Based Benzoxazines and Effect of Their Backbone Structure on Thermal and Flammability Properties of Polymers

Synthesis, Polymerization Kinetics and Thermal Properties of Benzoxazine Resin Containing ortho-Maleimide Functionality

Synthesis and Properties of 1,3,4-Oxadiazole-containing High-Performance Bismaleimide Resins

Novel Thermosetting Resins Based on 4-(N-maleimidophenyl)glycidylether: II. Bismaleimides and Polybismaleimides

Preparation And Characterization Of Novel Bismaleimide Resins Modified With Diallyl Bisphenol A

Synthesis, characterization, and thermal properties of benzoxazine monomers containing allyl groups

Film-forming Characteristics and Thermal Stability of Low Viscosity Benzoxazines Derived from Melamine

Synthesis and properties of a benzoxazine monomer containing maleimide and biphenyl groups

Synthesis of High Thermal Stability Polybenzoxazoles Via Ortho‐imide‐functional Benzoxazine Monomers

Synthesis and curing behavior of a novel benzoxazine-based bisphthalonitrile monomer

Synthesis of novel bismaleimide monomers based on fluorene cardo moiety and ester bond: Characterization and thermal properties

Synthesis and Thermal Properties of the Thermosetting Resin Based on Cyano Functionalized Benzoxazine

Synthesis, Properties of Novel Benzocyclobutene-Functionalized Siloxane Thermosets

Synthesis of Novel Imide-Functionalized Fluorinated Benzoxazines and Properties of Their Thermosets

Preparation and Properties of Novel Benzoxazine and Polybenzoxazine with Maleimide Groups

Trifunctional quinoxaline‐based maleimide and its polymer alloys with benzoxazine: Synthesis, characterization, and properties