A Guanidinium-Based Mn 4+ -Doped Red-Emitting Hybrid Phosphor with High Stability
Hong Ming,Yifei Zhao,Yayun Zhou,Shuai Zhang,Yuanjing Wang,Enhai Song,Zhiguo Xia,Qinyuan Zhang
DOI: https://doi.org/10.1021/acsaelm.0c00916
IF: 4.494
2020-12-09
ACS Applied Electronic Materials
Abstract:Great efforts have been put in search of phosphors to fulfill the requirements for phosphor-converted white light-emitting diodes (pc-WLEDs). Herein, a general organic–inorganic hybridization strategy was demonstrated in Mn<sup>4+</sup>-, Cr<sup>3+</sup>-, or Eu<sup>3+</sup>-doped guanidinium-based zero-dimensional hybrid fluorides to find phosphors for pc-WLEDs. Among which, GA<sub>3</sub>AlF<sub>6</sub>:Mn<sup>4+</sup> (where GA represents the guanidinium cation [C(NH<sub>2</sub>)<sub>3</sub>]<sup>+</sup>) was selected to reveal their crystal structure, local symmetry, and luminescence properties. Density functional theory calculations suggested that GA<sub>3</sub>AlF<sub>6</sub> with a wide band gap (∼5.24 eV) and the <i>F</i><sub class="stack">i</sub><sup class="stack">′</sup> interstitials are generated to balance the charge differences caused by non-equivalent doping. The GA<sub>3</sub>AlF<sub>6</sub>:Mn<sup>4+</sup> hybrid could sustain ∼573 K high temperature without degradation and keep 90.1% of the original luminescence intensity at ∼373 K. A pc-WLED with wide color gamut (108.3%) of National Television System Committee standard was fabricated with GA<sub>3</sub>AlF<sub>6</sub>:Mn<sup>4+</sup>, suggesting its potential in high-quality backlight displays. This work not only brings a brand-new kind of organic–inorganic fluoride phosphor family but also provides great guiding significance for future exploration of fluoride-based functional materials containing a hybrid structure.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaelm.0c00916?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaelm.0c00916</a>.Schematic diagram for the synthesis of GA<sub>3</sub>AlF<sub>6</sub>:Mn<sup>4+</sup> hybrid (Figure S1); XRD patterns, PLE and PL spectra, and PL decay curves of Mn<sup>4+</sup>-, Cr<sup>3+</sup>-, or Eu<sup>3+</sup>-doped organic–inorganic hybrid fluorides with the formula GA<i><sub>x</sub></i>BF<sub>6</sub> (<i>x</i> = 2, B = Si<sup>4+</sup>, Ge<sup>4+</sup>, or Ti<sup>4+</sup>; <i>x</i> = 3, B = Al<sup>3+</sup> or Ga<sup>3+</sup>) (Figures S2–S7); SEM image and the corresponding EDS of GA<sub>3</sub>AlF<sub>6</sub>:Mn<sup>4+</sup> (Figure S8); three possible Mn<sup>4+</sup>-doped structural models after structure optimization based on DFT calculation (Figure S9); PL spectra of GA<sub>3</sub>AlF<sub>6</sub>:Mn<sup>4+</sup> and the reference sample for QE (Figure S10); moisture resistance of the hybrid sample (Figure S11); stability of pc-WLED (Figure S12); nominal and actual doping amount of Mn<sup>4+</sup> suggested by the ICP-OES results (Table S1); Rietveld refinement crystal structure parameters of X-ray diffraction profiles of GA<sub>3</sub>AlF<sub>6</sub> (Tables S2 and S3); photoelectric properties of pc-WLEDs and their color gamut in the CIE 1931 color space (Table S4) (<a class="ext-link" href="/doi/suppl/10.1021/acsaelm.0c00916/suppl_file/el0c00916_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,engineering, electrical & electronic