Abstract:Novel low-cost Fe50-2xMn30Co10Cr10NixCux (x = 0, 5 at%) high-entropy alloys (HEAs) were produced by vacuum melting and then processed by the cyclic closed-die forging (CCDF) process. It was found that both the as-homogenized and CCDF-processed specimens primarily consisted of a single face-centered cubic (FCC) structure, and the severe plastic strain through CCDF did not result in phase transformations. The microstructure of the CCDF-processed Fe50Mn30Co10Cr10 alloy after the sixth pass demonstrated a uniform structure with ultrafine grains measuring 285 nm in size, whereas for the CCDF-processed Fe40Mn30Co10Cr10Ni5Cu5 alloy, the grain size was 135 nm, with a relatively uniform distribution. The CCDF-processed Fe50Mn30Co10Cr10 and especially the Fe40Mn30Co10Cr10Ni5Cu5 alloy exhibited significantly higher microhardness compared to the as-homogenized state, with microhardness values being 2.42 and 2.72 times higher, respectively. Furthermore, the wear test results indicated that the CCDF processing effectively increased the wear resistance of the alloys, which was attributed to the changes in morphology and distribution of as-cast dendrites, along with the grain refinement of the matrix phase during CCDF. The CCDF-processed Fe40Mn30Co10Cr10Ni5Cu5 alloy exhibited the lowest wear rate, i.e., (1.2 +/- 0.2) x 10(-5) mm(3).N-1.m(-1), whereas that for the Fe50Mn30Co10Cr10 alloy was (2.4 +/- 0.1) x 10(-5) mm(3).N-1.m(-1). Analysis of wear surfaces indicated that the wear mechanisms of the as-homogenized HEAs were adhesive wear and abrasive wear with some delamination, while plastic deformation and adhesive wear were significantly reduced in the CCDF-processed specimens, especially in the Fe40Mn30Co10Cr10Ni5Cu5 alloy. These findings suggest that CCDF has the potential to achieve cost-effective nanostructured HEAs and to implement them in engineering applications.

Microstructure and tribological properties of in-situ carbide/CoCrFeNiMn high entropy alloy composites synthesized by flake powder metallurgy

Robust wear performance of graphene-reinforced high entropy alloy composites

Microstructures and Wear Behaviour of (Fecocrni)1-X(wc)x High Entropy Alloy Composites

Microstructure, mechanical and tribological properties of oxide dispersion strengthened CoCrFeMnNi high-entropy alloys fabricated by powder metallurgy

Enhanced wearing resistance of carbide reinforced FeCoNiCrMn high entropy alloy prepared by mechanical alloying and spark plasma sintering

Metastable FeCrMnCo HEAs with the reinforcement of tungsten carbide fabricated by laser melting: Microstructure, mechanical properties and tribological behaviors

Effect of C additions to the microstructure and wear behaviour of CoCrFeNi high-entropy alloy

Microstructural and Tribological Characteristics of In Situ Induced Chrome Carbide Strengthened CoCrFeMnNi High-Entropy Alloys

Effect of carbon content on microstructure, hardness and wear resistance of CoCrFeMnNiCx high-entropy alloys

Strengthening the mechanical properties and wear resistance of CoCrFeMnNi high entropy alloy fabricated by powder metallurgy

Microstructures and mechanical properties of nano carbides reinforced CoCrFeMnNi high entropy alloys

Influence of Co Content on Cracking Behavior and Wear Resistance of WCp-Reinforced FeCrMnCox HEAs Fabricated by the Laser Cladding Method

Microstructure Refinement and Wear Resistance Enhancement of Cost-Effective Fe50−2xMn30Co10Cr10NixCux (x = 0, 5 At.%) High-Entropy Alloys Through Cyclic Closed-Die Forging Process

Realizing high strength and toughness of gradient high-entropy alloy coating by in-situ interface reaction of FeCoCrNi/FeCoCrAl

In Situ Development and High Temperature Features of CoCrFeNi-M6Cp High Entropy-Alloy Based Hardmetal

Effect of graphene oxide on CoCrFeNi high-entropy alloy coatings prepared by the electrodeposition method

Mechanical properties and wear behaviors of FeCoNiCrMnTix high-entropy alloys manufactured by vacuum arc melting

Microstructure and mechanical properties of Al-Fe-Co-Cr-Ni high entropy alloy fabricated via powder extrusion

Microstructural characteristics and enhanced wear resistance of nanoscale Al<sub>2</sub>O<sub>3</sub>/13 wt%TiO<sub>2</sub>-reinforced CoCrFeMnNi high entropy coatings

Effects of Ni/MoS2, Ag and Cr2O3 on the Microstructure and Mechanical Performance of a CoCrFeNi High-Entropy Alloy over a Wide Temperature Range

Microstructure evolution and high temperature wear resistance of in-situ synthesized carbides reinforced NiCoFeCrSiMo high entropy alloy coatings fabricated by laser cladding