Ultimate Resourcization of Waste: Crab Shell-Derived Biochar for Antimony Removal and Sequential Utilization as an Anode for a Li-Ion Battery
Xinyue Zhang,Yao Wang,Na Ju,Yongjian Ai,Yangyang Liu,Jiaxing Liang,Ze-Nan Hu,Rongxiu Guo,Wenjuan Xu,Wei Zhang,Yang Qi,Dun Niu,Qionglin Liang,Hong-bin Sun,Yang Yang
DOI: https://doi.org/10.1021/acssuschemeng.1c01851
2021-06-23
Abstract:The development of high-capacity adsorbents is pivotal for the removal of antimonite (Sb(III)) and antimonate (Sb(V)) as priority pollutants in water. Herein, a Fe-La-doped biomass carbon adsorbent (Cs/Fe-La) was prepared for efficient removal of both Sb(III) and Sb(V). Cs/Fe-La shows excellent adsorption behavior for both Sb(III) and Sb(V) at 40 °C with a maximum capacity of 498 and 337 mg/g, respectively. Additionally, the antimony adsorption mechanism and the contribution of Cs/Fe-La composition to high capacity were analyzed based on the characterization of physicochemical analysis and adsorption studies, and the pseudo-second-order kinetic model as well as the Langmuir model fit the results well. Remarkably, considering the secondary pollution caused by direct disposal of antimony-containing waste adsorbents, an antimony-enriched waste adsorbent (Cs/Fe-La-SbO<i><sub>x</sub></i>) was used as an anode material for a Li-ion battery. The heat-treated waste adsorbent exhibited good cycling performance with a reversible specific capacity of 833.8 mAh/g after 500 cycles. This work has demonstrated a promising pathway that can achieve the removal and sustainable utilization of antimony simultaneously by minimizing antimony contamination and maximizing the recycling of antimony-enriched adsorbents.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.1c01851?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.1c01851</a>.The preparation of adsorbents and anode materials in a Li-ion battery; equations of adsorption experiments; SEM images of the crab shell before and after removal of Ca and corresponding EDS; nitrogen adsorption/desorption isotherms and pore-size distribution (inset) of Cs/Fe-La; the TGA curve of Cs/Fe-La; XPS survey spectra of Cs/Fe-La before and after adsorption; the summarization table of pseudo-first-order and pseudo-second-order kinetics and intraparticle diffusion model constants for Sb(III) and Sb(V) adsorption, adsorption isotherm constants for Sb(III) and Sb(V) adsorption, and the parameter of <i>R</i><sub>L</sub> from the Langmuir model; the diagram of the fixed bed; and performance of Cs/Fe-La as Li-ion battery anodes, including CV curves, discharge/charge profiles, rate performance, and the Nyquist diagram (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.1c01851/suppl_file/sc1c01851_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology