Abstract:The hot deformation behavior of a FeCoCrNi high-entropy alloy was investigated in this work. The tests were carried out at 900–1100 o C, under strain rates of 0.001–0.1 s -1 and the effect of friction between specimen and tool on flow stress curves under different deformation conditions was analyzed and modified. The experimental results were employed to determine the constitutive equation with strain-dependent material constants for modeling and for prediction of flow stress at different deformation conditions, using the data obtained from the Sellars–Tegart–Garofalo equation. Microstructural studies revealed that dynamic recrystallization was the primary softening mechanism, resulting in significant microstructural reconstitution and fine grains formation. A complete-recrystallized microstructure with a high proportion of annealing twin boundary was obtained in the specimen hot compressed at 1000 o C/0.01 s -1 , so that the average grain size was 22 μm, compared to the initial grain size of 42 μm. The increase of the size and fraction of the DRXed grains during hot deformation decrease the alloy hardness. The dynamic recrystallization parameters such as critical, peak, and steady-state stress, and strain were determined using the work hardening rate analysis. Moreover, the activation energy for deformation of the alloy was determined to be 417 kJ mol -1 . The results also indicated that the critical stress and strain for initiating dynamic recrystallization were inversely proportionate to deformation temperature and the strain rate. Furthermore, increasing the deformation temperature resulted in grain growth, whereas increasing the strain rate led to grain refinement. The critical stress and strain were dependent on the Zener–Hollomon ( Z ) parameter via a power relation with exponents of 0.14 and 0.12, respectively.

Mechanical Behavior of Al0.5CoCrFeNi HEA During Warm Deformation

Microstructural Evolution and Elevated-Temperature Strengthening Mechanism of Co-free FeCrMnNiV0.2Alx High-Entropy Alloys During Annealing

Microstructural Evolution and Mechanical Properties of Al0.5CoCrFeNi High-Entropy Alloy after Cold Rolling and Annealing Treatments

Deformation mechanisms of Al0.1CoCrFeNi at elevated temperatures

Microstructural Evolution and Mechanical Properties of Al0.3CoCrFeNiSix. High-Entropy Alloys Containing Coherent Nanometer-Scaled Precipitates

High temperature deformation mechanism and microstructural evolution of relatively lightweight AlCoCrFeNi high entropy alloy

Microstructural Evolution and Tensile Properties of Al0.3CoCrFeNi High-Entropy Alloy Associated with B2 Precipitates

Temperature-dependent mechanical behavior of an Al 0.5 Cr 0.9 FeNi 2.5 V 0.2 high-entropy alloy

Deformation Behavior and Processing Map of AlCoCrFeNiTi0.5 High-Entropy Alloy at High Temperature

Constitutive equation and microstructure analysis of Al0.6CoCrFeNi high entropy alloy during hot deformation

High temperature deformation behavior of dual-phase Al0.6CoCrFeNi high-entropy alloys

Hot deformation behavior and mechanism of cold deformed CoCrCu1.2FeNi high entropy alloy

Elucidating the warm compression of CoCrCuFeNi high entropy alloy: Modeling and microstructural evolution

Dynamic Recrystallization Behavior of the Equiatomic FeCoCrNi High-Entropy Alloy during High Temperature Deformation

Tensile Properties and Serrated Flow Behavior of As-Cast CoCrFeMnNi High-Entropy Alloy at Room and Elevated Temperatures

Effects of Cr Content on Microstructure and Mechanical Properties of Co-Free FeCryNiAl0.8 High-Entropy Alloys

Effect of temperature on mechanical properties of Al0.5CoCrCuFeNi wrought alloy

Exploring hot deformation behavior of equimolar CoCrFeNi high-entropy alloy through constitutive equations and microstructure characterization

Hot Deformation Characteristics and Microstructure Evolution of CoCrFeNiZr0.3 Hypoeutectic High-Entropy Alloy

Effect of Heat Treatment on the Microstructure and Mechanical Properties of the Al0.6CoCrFeNi High-Entropy Alloy

Unleashing the microstructural evolutions during hot deformation of as-cast AlCoCrFeNi 2.1 eutectic high entropy alloy