Abstract:Silicon (Si) wafer is generally used as the substrate for structural analysis and residual stress measurement of thin coatings. A few studies can be found for mechanical and tribological characterization wherein Hertzian contact stress never exceeded 1 GPa. Si, being single crystal, pure, and having low surface roughness (R a ) is an ideal potential candidate for thin coating analysis. However, Si wafer breaks immediately under higher contact stress. The current study aims to push the contact stress limit to test thin coatings on Si wafer especially for friction and wear testing. To serve the purpose, different bias DLC coatings (−120 V, −80 V, −40 V, ZeroV, +40 V, +80 V, +120 V) were deposited on Si wafer employing closed field unbalanced magnetron sputtering (CFUMS) system. Using conveniently available experimental approach, Hertzian contact stress in tribological tests has been pushed up to 2.6 GPa successfully on DLC coated Si wafer. Thus, it is feasible to test thin coatings on Si wafer at high contact stress which will provide useful and consistent friction and wear data such that further test using the steel substrate will be reduced by a significant margin. A thorough mechanical, tribological and structural (Raman) analysis is presented. It was found that −120 V possessed the highest hardness (H: 17.6 GPa), modulus (E: 184 GPa) and residual stress (4.5 GPa). The same coating produced the lowest sp 2 /sp 3 ratio, wear rate using contact stress (0.092 × 10 −13 mm 4 /N) and wear/friction energy (0.071 × 10 −13 mm 3 /J 2 ) in comparison to other coatings used in the study. Counter body analysis for −120 V shows the minimum scratch area depicting friction between transfer film and DLC hence the lowest coefficient of friction (0.061) was obtained. Moreover, surface topography is explained with the aid of atomic force microscope (AFM) images and surface roughness (R a ) data. AFM revealed craters and bumpy like surfaces for positive and negative biased samples respectively.

Residual stress and tribological behavior of hydrogen-free Al-DLC films prepared by HiPIMS under different bias voltages

Hydrogen-free DLC films fabricated using superimposed HiPIMS-DCMS deposition system: Bias voltage effects

Tribological Properties of Diamond-Like Carbon Films Deposited by Vacuum Arc

Effect of bias gradient delta on mechanical and tribological properties of DLC films sputtered on ACM

Improved mechanical and tribological properties of diamond-like carbon films by adjusting pulsed substrate bias

Influence of bias patterns on the tribological properties of highly hydrogenated PVD a-C:H films

Microstructure, mechanical, and wettability properties of Al-doped diamond-like films deposited using a hybrid deposition technique: Bias voltage effects

Effect of the bias-graded increment on the tribological and electrochemical corrosion properties of DLC films

The Effect of Applied Substrate Negative Bias Voltage on the Structure and Properties of Al-containing A-C:H Thin Films

Experimental study and influence mechanismof the properties of α-C:H thin film at different bias voltages

Influences of Bias Voltage on Mechanical and Tribological Properties of Ti–Al–C Films Synthesized by Magnetron Sputtering

Effects of Bias Voltage on Structure and Properties of Tial-Doped A-C:H Films Prepared by Magnetron Sputtering

The effects of Cr and B doping on the mechanical properties and tribological behavior of multi-layered hydrogenated diamond-like carbon films

Mechanical and corrosion properties of hydrogen-free DLC coatings prepared on degradable as-extruded WE43 alloy using FCVA technology

Silicon wafer as a feasible candidate for tribological characterization of thin coatings under high contact stress?

Mechanical and tribological properties of non-hydrogenated DLC films synthesized by IBAD

Influence of Nitrogen Content and Bias Voltage on Residual Stress and the Tribological and Mechanical Properties of CrAlN Films

Microstructure, mechanical and tribological properties of multilayer Ti-DLC thick films on Al alloys by filtered cathodic vacuum arc technology

Effect of sp3 Content on Adhesion and Tribological Properties of Non-Hydrogenated DLC Films

The Effect of Gradient Bias Design on Electrochemistry and Tribology Behaviors of PVD CrN Film in a Simulative Marine Environment

Vacuum tribological properties in Cr-doped H-DLC self-lubricating radial spherical plain bearings