Abstract:Microwave (MW) treatment was reported as an efficient method to prepare porous carbon-based electrode material with high capacity for a high-performance supercapacitor. Herein, the superiority of the mechanism of MW treatment was tried to be revealed by preparing a N and O co-doped porous activated carbon (MWAC) based on a heteroatom-rich corn cob and compared to that of the conventional heating method. The resulting MWAC has a large specific surface area of 2508 m<sup>2</sup>/g with hierarchical micro- and mesoporous structures and abundant heteroatom doping of O and N. In a three-electrode system, the MWAC shows a superior specific capacitance of 560 F/g at a discharge current density of 0.5 A/g in a 6 mol/L KOH aqueous electrolyte. The symmetric supercapacitor fabricated by MWAC electrodes in a 6 mol/L KOH electrolyte shows excellent capacity retention of 96.8%, even after 10 000 galvanostatic charge–discharge cycles at the current density of 1 A/g. The aqueous (6 mol/L KOH) symmetric supercapacitor delivers a high energy density of 9.24 Wh/kg at a power density of 250 W/kg. The results prove that the MW heating shows more superiority in retaining inherent heteroatoms and creating hierarchical micro- and mesoporous structures of activated carbon for supercapacitors with high performance.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.1c00337?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.1c00337</a>.Systematic condition optimization experiments for the preparation of MWAC, including MW power, activation time, and mass ratio of C/KOH (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.1c00337/suppl_file/ef1c00337_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Rapid preparation of P/O doped nano-porous carbon by microwave method for high-performance supercapacitors

Highly N/O co-doped ultramicroporous carbons derived from nonporous metal-organic framework for high performance supercapacitors

Highly Active N, O-doped Hierarchical Porous Carbons for High-Energy Supercapacitors

Hydrangea-like N/O codoped porous carbons for high-energy supercapacitors

Fast microwave self-activation from chitosan hydrogel bead to hierarchical and O, N co-doped porous carbon at an air-free atmosphere for high-rate electrodes material

Fabrication of self-doped aramid-based porous carbon fibers for the high-performance supercapacitors

Microwave-Assisted Preparation of Hierarchical N and O Co-Doped Corn-Cob-Derived Activated Carbon for a High-Performance Supercapacitor

A micropore-dominant N,P,S-codoped porous carbon originating from hydrogel for high-performance supercapacitors mediated by phytic acid

Oxygen/phosphorus co-doped porous carbon from cicada slough as high-performance electrode material for supercapacitors

Preparation of N/O co-doped porous carbon by a one-step activation method for supercapacitor electrode materials

Oxygen Self-doped Hierarchical Porous Carbons Derived from Coal Liquefaction Residue for High-performance Supercapacitors in Organic and Ionic Liquid-based Electrolytes

Nitrogen and Phosphorus Co-doped Porous Carbon for High-Performance Supercapacitors

N-O-P co-doped porous carbon aerogel derived from low-cost biomass as electrode material for high-performance supercapacitors

A combination of heteroatom doping engineering assisted by molten salt and KOH activation to obtain N and O co-doped biomass porous carbon for high performance supercapacitors

Sub-nanopores-containing N,O-codoped porous carbon from molecular-scale networked polymer hydrogel for solid-state supercapacitor

Chitosan-Based Synthesis of O, N, and P Codoped Hierarchical Porous Carbon as Electrode Materials for Supercapacitors

Porous Carbon Electrode from Starch Soluble for Realizing High‐Performance Supercapacitor

Synthesis and electrochemical study of phosphorus-doped porous carbon for supercapacitor applications

Powerful puffing carbonization pretreatment prepared porous carbon for high-performance supercapacitors

N/O Co-doped Porous Carbon with Controllable Porosity Synthesized via an All-in-One Step Method for a High-Rate-Performance Supercapacitor

An environmentally friendly process to derive N/O/S-codoped porous carbon from biomass waste with high yield for high performance supercapacitor