Effect of short-chain branches in high-molecular-weight component on tensile properties of polyethylene solids

Takumitsu Kida,Ryo Tanaka,Takeshi Shiono,Hiroki Takeshita,Katsuhisa Tokumitsu

DOI: https://doi.org/10.1016/j.polymer.2024.126906

IF: 4.6

2024-03-15

Polymer

Abstract:The effects of short-chain branches (SCBs) in the high-molecular-weight (MW) chains on the solid-state tensile properties of polyethylene (PE) have been investigated using blend samples of linear PE with a polydisperse MW distribution and PE with very narrow MW distribution and SCBs with four carbons. The introduction of SCBs in the high-MW chains had almost no effect on the crystalline structure, but relaxation of the interlamellar amorphous chains was only activated by blending the high-MW chains with a large fraction of SCBs (2.0 wt%). The blends of PE with 0.4 wt% SCBs resulted in significant increases in the strain-hardening modulus and strength without greatly decreasing the strain at break. The improvement in the strain-hardening modulus and strength by adding a small amount of SCBs (0.4 wt%) was significant compared with the improvement by adding linear PE or branched PE with a large amount of SCBs (2.0 wt%). For a small amount of SCBs, the SCBs will be incorporated into the crystalline structure, which enhances the fragmentation and subsequent orientation of the crystalline structure under yielding deformation. Consequently, blending the branched PE with a small amount of SCBs in the high-MW chains leads to significant improvement of the tensile properties.

polymer science