Sintering, thermal expansion, and thermal transport properties of A4Ta2O9 (A= Ca, Mg) tantalates

Keren Luo,Lin Chen,Baihui Li,Liang Lv,Yuncheng Wang,Xiaolan Ji,Haitao Yun,Jing Feng

DOI: https://doi.org/10.1016/j.ceramint.2022.04.331

IF: 5.532

2022-08-15

Ceramics International

Abstract:Searching for new oxides with low thermal conductivity and high thermal expansion coefficients (TECs) as thermal barrier coatings (TBCs) is vital for the development of highly efficient gas turbines and aeroengines. We report the densification sintering, high TECs, and low thermal conductivity of A4Ta2O9 (A = Ca, Mg) tantalates. The best sintering temperature of dense A4Ta2O9 ceramics was determined via an optical contact angle tester, and samples with a relative density of 99.8% were synthesized via spark plasma sintering (SPS). The hardness (9–10 GPa), Young's modulus (172.7–211.8 GPa) and fracture toughness (1.5–1.6 MPa m1/2) of the A4Ta2O9 ceramics are primarily affected by the bonding strength. Furthermore, we studied the thermal transport properties of A4Ta2O9. The low thermal conductivity (1.78–1.93 W m−1 K−1 at 900 °C), extraordinary phase stability, and high TECs (11.4–11.8 × 10−6 K−1 at 1200 °C) of A4Ta2O9 ceramics make them candidate TBCs with high operating temperatures.

materials science, ceramics