High-temperature corrosion mechanism of a promising scandium tantalate ceramic for next generation thermal barrier coating under molten calcium–magnesium-aluminosilicate (CMAS)

Fuxing Ye,Yihui Yuan,Shuai Yan,Lei Guo,Jianxing Yu
DOI: https://doi.org/10.1016/j.matchemphys.2020.123679
IF: 4.778
2020-12-01
Materials Chemistry and Physics
Abstract:<p>Hot corrosion caused by molten calcium–magnesium-aluminosilicate (CMAS) is one of the significant failure factors of thermal barrier coating (TBC). Scandium tantalite (ScTaO<sub>4</sub>) is expected to be a next generation of TBC material because of its great thermophysical characteristics. This study focused on high-temperature corrosion behaviors of ScTaO<sub>4</sub> ceramic exposure to molten CMAS at 1300 °C. During corrosion experiments, a clear but discontinuous reaction layer containing CaTa<sub>2</sub>O<sub>6</sub> and Sc<sub>2</sub>SiO<sub>5</sub> was observed, which was formed by dissolution reprecipitation. In addition, ScTaO<sub>4</sub> showed good phase stability and maintained monoclinic wolframite structure with P2/c (13) space group in the corrosion tests. Moreover, Ca, Mg and Al were all kept away from the ScTaO<sub>4</sub> ceramic due to low solubility of Sc<sup>3+</sup> in the CMAS. Therefore, ScTaO<sub>4</sub> ceramic owns great ability to resist the corrosion of CMAS. Good phase stability enables ScTaO<sub>4</sub> to stably exist at high temperature, reducing volume change, thus extending the service life of the coating. Meanwhile, great corrosion resistance of CMAS reduces the consumption of ScTaO<sub>4</sub> under adverse environmental conditions, further extending the service life of the coating. In summary, ScTaO<sub>4</sub> is a new kind of potential thermal barrier material to replace YSZ ceramic.</p>
materials science, multidisciplinary
What problem does this paper attempt to address?
The paper aims to investigate the corrosion behavior and mechanisms of scandium tantalate (ScTaO₄) ceramics in molten calcium magnesium aluminosilicate (CMAS) at high temperatures. The main objective is to evaluate the potential of ScTaO₄ as a next-generation thermal barrier coating material, especially under high-temperature conditions of 1300°C. The study found that ScTaO₄ exhibits excellent thermophysical properties and phase stability, and demonstrates good corrosion resistance to CMAS at high temperatures. This makes ScTaO₄ a strong candidate to replace traditional yttria-stabilized zirconia (YSZ) thermal barrier coating materials.