Fabrication of Pd/CeO 2 nanocubes as highly efficient catalysts for degradation of formaldehyde at room temperature

Yafeng Chen,Guimin Jiang,Xiangzhi Cui,Zuotai Zhang,Xinmei Hou

DOI: https://doi.org/10.1039/d1cy00766a

2021-01-01

Abstract:The highly active Pd/CeO 2 nanocube interface guarantees a high percentage of metallic Pd and the surface active O species is responsible for the complete decomposition of formaldehyde.

chemistry, physical

What problem does this paper attempt to address?

High Surface Area Au/CeO2 Catalysts for Low Temperature Formaldehyde Oxidation

Hong-Fang Li,Na Zhang,Ping Chen,Meng-Fei Luo,Ji-Qing Lu

DOI: https://doi.org/10.1016/j.apcatb.2011.09.013

2011-01-01

Abstract:Gold catalysts supported on high surface area CeO2 were synthesized and tested for low temperature formaldehyde oxidation. It was found that the reactivity was greatly enhanced by increasing surface area of the support. Complete conversion of formaldehyde was obtained on a 3.0Au/CeO2-270 catalyst with a surface area of 270m2g−1 at 50°C, and a conversion of 92.3% was obtained at 37°C over the same catalyst, which made it promising for indoor formaldehyde removal. Detailed characterizations of the catalyst showed that the enhancement could be attributed to two factors. One was that Au species mainly in high oxidation states formed on the high surface area CeO2 resulted in a high degree of HCHO adsorption, as revealed by in situ diffuse reflectance infrared Fourier transform spectroscopy. The other was the high surface area CeO2 provided more oxygen vacancies by the nano effect and the formation of AuxCe1−xO2−δ solid solution as revealed by Raman spectroscopy, on which oxygen molecules could be transformed to active species for the reaction.
Highly efficient formaldehyde elimination over meso-structured M/CeO2 (M = Pd, Pt, Au and Ag) catalyst under ambient conditions

gengnan li,liang li

DOI: https://doi.org/10.1039/c5ra04928h

IF: 4.036

2015-01-01

RSC Advances

Abstract:A series of mesoporous CeO2 supported noble metal (Pt, Pd, Au and Ag) catalysts, fabricated through a facial pyrolysis and in situ reduction protocol, were used for formaldehyde elimination under ambient conditions. The materials possessed relatively high specific surface area and uniformly dispersed noble metal nanoparticles, and showed very high catalytic activities for formaldehyde oxidation. For about 1 wt% noble metal loaded materials, Pt/CeO2, Pd/CeO2 and Au/CeO2 catalysts could completely catalytically oxidize HCHO at room temperature. Even for the low activity Ag/CeO2 catalyst, the complete conversion temperature could reach 100 degrees C, much lower than that reported before. Such good catalytic properties could be attributed to the strong synergetic interaction between the active component and CeO2 nano-crystalline aggregated support. The reaction mechanism over the noble-metal/CeO2 catalyst was also discussed through in situ DRIFTS analysis.
Efficient Removal Of Formaldehyde By Nanosized Gold On Well-Defined Ceo2 Nanorods At Room Temperature

Quanlong Xu,Wanying Lei,Xinyang Li,Xiaoying Qi,Jiaguo Yu,Gang Liu,Jinlong Wang,Pengyi Zhang

DOI: https://doi.org/10.1021/es5019477

IF: 11.4

2014-01-01

Environmental Science & Technology

Abstract:Gold (Au) nanoparticles (NPs) supported on well-defined ceria (CeO2) nanorods with exposed {110} and {100} facets were prepared by a deposition-precipitation method and characterized by powder X-ray diffraction, micro-Raman spectroscopy, X-ray photoelectron spectroscopy, nitrogen adsorption-desorption, transmission electron microscopy, high-resolution transmission electron microscopy, and high-angle annular dark-field scanning transmission electron microscopy. Both nanometer and subnanometer gold particles were found to coexist on ceria supports with various Au contents (0.01-5.4 wt %). The catalytic performance of Au/CeO2 catalysts was examined for formaldehyde (HCHO) oxidation into CO2 and H2O at room temperature and shown to be Au content dependent, with 1.8 wt % Au/CeO2 displaying the best performance. On the basis of the results from hydrogen temperature-programmed reduction and in situ Fourier transform infrared spectroscopy observations, the high reactivity and stability of Au/CeO2 catalysts is mainly attributed to the well-defined ceria nanorods with {110} and {100} facets which present a relatively low energy for oxygen vacancy formation. Furthermore, gold NPs could induce the weakened Ce-O bond which in turn promotes HCHO oxidation.
Highly dispersed Fe-Ce mixed oxide catalysts confined in mesochannels toward low-temperature oxidation of formaldehyde

Jianwei Fan,Xufei Niu,Wei Teng,Peng Zhang,Wei-xian Zhang,Dongyuan Zhao

DOI: https://doi.org/10.1039/d0ta05473a

IF: 11.9

2020-01-01

Journal of Materials Chemistry A

Abstract:Catalytic oxidation of formaldehyde (HCHO) is regarded as a promising strategy to eliminate this indoor air pollutant. The design of a highly active and cost-effective catalyst is still pivotal to improve the performance for HCHO oxidation. Herein, we report an Fe-Ce-O solid solution catalyst supported on ordered mesoporous silica (SBA-15) prepared by simple two-step impregnation-calcination, achieving highly efficient HCHO elimination at a low temperature. This strategy brings about the formation of small solid solution nanoparticles (7-12.9 nm) with good dispersion in confined spaces. Meanwhile, the catalysts possess large surface areas (similar to 500 m(2)g(-1)) and pore volumes (0.5 cm(3)g(-1)) with a pore size of similar to 7.5 nm. The results show that Fe content and calcination temperature have great effects on the generation of oxygen vacancies in the catalyst, and further on the catalytic performance. The 20% FeOx-CeOx/SBA-15-350 catalyst displays superior catalytic activity with 65% and 94.9% conversion at 30 degrees C and 60 degrees C with a low concentration of HCHO (9.8 mu g L-1), respectively, comparable to that for many reported precious metal catalysts. The high ratio of Ce(3+)due to the formation of an Fe-Ce-O solid solution and highly dispersed active sites by the spatial confinement is favorable for more oxygen vacancy generation, which mainly contributes to the excellent performance. This work opens up an avenue to design highly efficient non-noble metal nanocatalysts for volatile organic compound (VOC) elimination.
Efficient activation of Pd/CeO2 catalyst by non-thermal plasma for complete oxidation of indoor formaldehyde at room temperature

Kai Li,Jian Ji,Haibao Huang,Miao He

DOI: https://doi.org/10.1016/j.chemosphere.2019.125762

IF: 8.8

Chemosphere

Abstract:Formaldehyde is a typical indoor air pollutant and its removal is essential to protect human health and meet environmental regulations. Efficient activation of Pd/CeO2 catalyst by non-thermal plasma was investigated to achieve complete oxidation of formaldehyde at room temperature. The catalyst exhibited better activity and stability than conventional thermal reduced sample. Its HCHO conversion to CO2 kept at over 80% during 300 min test at a gas hourly space velocity of 150, 000 mL/g/h and HCHO concentration of 100 ppm. While the conversion dropped from 70% to 50% within 300 min test for the sample reduced at 300 °C. Compared with thermal reduced catalyst, plasma reduced sample exhibited more abundant surface active oxygen species, smaller palladium particle size and narrower particle size distribution. Moreover, palladium particles were partial covered by ceria layer for thermal reduced sample. Although strong interaction between palladium and ceria could be formed, the loss of metallic palladium occurs and hence the oxygen activation and mobility abilities are blocked. In situ DRIFTs results suggested that the intermediates over Pd/CeO2 catalyst were mainly formate, dioxymethylene and polyoxymethylene species, and the formate oxidation into CO2 process was highly promoted in the presence of water.
One-step fabrication of Pd-embedded hierarchically porous carbon micro-spheres for formaldehyde removal under mild conditions

Zhigang Ren,Peng Zhao,Ye Zhang,Yu Yang,Xiaoxuan Lyu,Chunxiang Lu

DOI: https://doi.org/10.1039/d1nj00198a

IF: 3.3

2021-01-01

New Journal of Chemistry

Abstract:Using the enclosed space of Pickering emulsion droplets as a template, we adopted a one-step strategy to prepare Pd and N co-doped multi-core layered porous carbon microspheres (Pd@NCMs-T) for room-temperature catalytic oxidation of HCHO.

chemistry, multidisciplinary
Construction of strongly-coupled CeO 2 /MnO 2 heterogeneous catalysts for highly-efficient removal of formaldehyde

Shuaishuai Zhang,Lingling Zhang,Li Liu,Xiang Chu,Xiao Wang,Shuyan Song,Hongjie Zhang

DOI: https://doi.org/10.1039/d3nj00810j

IF: 3.3

2023-03-12

New Journal of Chemistry

Abstract:Formaldehyde (HCHO) is highly toxic, but its low-temperature elimination is still a pressing challenge nowadays. In this work, we demonstrate an interface engineering strategy to boost the catalytic performance of the promising MnO 2 catalysts by coupling the CeO 2 promoters on the surface. The as-prepared CeO 2 –MnO 2 mixed-metal oxide (CeMn- x ( x = 0.1, 0.5, and 1)) catalysts with a Ce/Mn ratio of 0.5/10 possess excellent catalytic activity and a relatively low T 100 (the temperature for 100% HCHO conversion) of 95 °C is achieved. More oxygen vacancies, outstanding redox ability, and the strong interaction between CeO 2 and MnO 2 are responsible for the enhanced catalytic activity of CeMn. This study provides novel insight into the design of MnO x catalysts for the purification of HCHO at low temperatures.

chemistry, multidisciplinary
The composite of UiO-66 derived ZrO2 and g-C3N4 for oxidative removal of formaldehyde at the room temperature

Jihai Duan,Xin He,Xianxin Fang,Jin Yue,Guanghui Chen,Weiwen Wang

DOI: https://doi.org/10.1016/j.diamond.2022.109365

IF: 3.806

2022-11-01

Diamond and Related Materials

Abstract:Formaldehyde (HCHO) is a common indoor organic pollutant, which causes serious damage to people's health. The removal of formaldehyde is a difficult problem that human beings have to face in healthy life. MOF derivatives are a research hotspot in the field of catalysis in recent years. In this paper, a UiO-66 derived ZrO2 was selected for the study of formaldehyde degradation. Combining ZrO2 and g-C3N4 through multiple calcinations, a heterostructure was successfully constructed, which enabled the catalyst to absorb visible light. Then supported Ag by photoreduction can further improve the dispersibility and visible light absorption ability of the catalyst. When the addition amount of ZrO2 is 300 mg, Ag@g-C3N4/ZrO2-300 degrades 81.3 % of formaldehyde after 3 h of illumination and exhibits excellent stability. This work provides a certain reference value for the application of MOF and its derivatives in the field of formaldehyde degradation.

materials science, multidisciplinary,physics, applied, condensed matter, coatings & films
Ag/Ceo2 Nanospheres: Efficient Catalysts for Formaldehyde Oxidation

Lei Ma,Dingsheng Wang,Junhua Li,Bingyang Bai,Lixin Fu,Yadong Li

DOI: https://doi.org/10.1016/j.apcatb.2013.10.039

2014-01-01

Abstract:Ag/CeO2 nanosphere catalysts, prepared by a one-step hydrothermal method, were used to eliminate the indoor formaldehyde (HCHO) pollution. The activity test results showed that Ag/CeO2 nanosphere catalysts exhibited much higher catalytic activity than normal Ag/CeO2 particles prepared by conventional impregnation method. Ag/CeO(2)nanosphere catalysts could reach complete HCHO oxidation above 110 degrees C under relatively high space velocity. The specific reaction rate per second and per unit of surface area of Ag/CeO2 nanosphere catalysts were almost 3.6 times higher than normal Ag/CeO2 particle catalysts at 110 degrees C. The prepared catalysts were also characterized by various methods. HRTEM, BET, and XRD results showed that Ag/CeO2 products were nanosphere shapes with average sizes around 80-100 nm, and were comprised of many small particles with a crystallite size of 2-5 nm. Cerium and silver were well distributed throughout the individual Ag/CeO2 nanosphere crystal. According to the results in XPS, H-2-TPR, O-2-TPD, and Raman spectra, surface chemisorbed oxygen easily formed on the Ag/CeO2 nanosphere catalysts. The synergetic interaction might exist between Ag and CeO2 nanosphere, and the presence of silver could facilitate surface chemisorbed oxygen activation, which mainly contributed to the HCHO oxidation. Based on In-situ DRIFTS results, formate species (HCOO-) were found to be the key intermediates and be activated on the surface active oxygen of Ag/CeO2 nanosphere catalysts in the catalytic oxidation process of HCHO, which would be further oxidized into the final product water and carbon dioxides. (C) 2013 Elsevier B.V. All rights reserved.
Photocatalytic Degradation of Gaseous Formaldehyde by Fe-Doped ZnO Nanorods Grown on Ceramic Spheres

Duan Yue-Qin,Yang Song-Po,Yu Jiang-Ling,Yuan Zhi-Hao

DOI: https://doi.org/10.11862/cjic.2014.184

2014-01-01

Abstract:Zinc oxide (ZnO) and Fe doped ZnO nanorods were fabricated on ceramic balls by a simple low cost wet-chemical route. The as-prepared samples were characterized by XRD, SEM, TEM and UV-Vis spectroscopy. Photocatalytic activities of pure ZnO and Fe doped ZnO nanorods were investigated for degradation of formaldehyde gas under UV irradiation. The results show that doped catalyst exhibits superior photocatalytic performance than that of pure ZnO nanorods and 4% Fe doping catalyst displays the optimal photoactivity. The catalyst has good stability and is easy to be recoverd. The catalytic efficiency still maintains 85% after 10 cycls.
Preparation of porous MnO2/CeO2 composite for the effective removal of formaldehyde from air

Xing Li,Jun Li,Xixian Yang,Lisheng Deng,Tao Zeng,Hongyu Huang

DOI: https://doi.org/10.1016/j.materresbull.2022.111751

IF: 5.6

2022-06-01

Materials Research Bulletin

Abstract:A porous MnO2/CeO2 composite catalyst was prepared via the template method for the catalytic decomposition of formaldehyde (HCHO). The physical and chemical properties of the catalysts were intensively characterized via X-ray diffraction, transmission electron microscopy, Brunauer-Emmett-Teller analysis, temperature programmed reduction system and X-ray photoelectron spectroscopy. The catalytic activity and stability for HCHO oxidation were measured via a fixed bed reactor, and the effects of physical and chemical properties of the catalysts on their catalytic performance were investigated. The results showed that the porous MnO2/CeO2 catalyst had abundant 3D pore structures, a large specific surface area, an amorphous structure, and an abundance of lattice oxygen species. Thus, the MnO2/CeO2 catalyst had high catalytic activity and stability for HCHO decomposition. This catalyst completely decomposed HCHO at 90 °C and maintained a 99% HCHO conversion rate over 72 h. The highly porous structure reduced the diffusion resistance in the reaction process and improved the efficiency of catalytic decomposition of HCHO. Doping with CeO2 improved the low temperature oxidation activity and catalytic stability of the porous MnO2/CeO2 catalyst. The porous MnO2/CeO2 composite was an effective agent for the removal of harmful HCHO from the air.

materials science, multidisciplinary
Three-dimensionally ordered macroporous Au/CeO 2-Co 3O 4 catalysts with nanoporous walls for enhanced catalytic oxidation of formaldehyde

Baocang Liu,Yang Liu,Changyan Li,Wenting Hu,Peng Jing,Qin Wang,Jun Zhang

DOI: https://doi.org/10.1016/j.apcatb.2012.08.005

2012-01-01

Abstract:Three-dimensionally ordered macroporous (3DOM) Au/CeO2-Co3O4 catalysts were created via a precursor thermal decomposition-assisted colloidal crystal templating method. The 3DOM Au/CeO2-Co3O4 catalysts possessed well-defined 3DOM structures with adjustable pore sizes, and their compositions, phase structures, and surface elemental valence states can be well controlled by solely adjusting the Ce/Co molar ratio. Moreover, the nanoporous walls with pore sizes around ∼3–4nm were created in 3DOM Au/CeO2-Co3O4 catalysts through the thermal decomposition of Co and Ce oxalate precursors during the preparation. The 3DOM Au/CeO2-Co3O4 catalysts exhibited superior catalytic activity for formaldehyde (HCHO) catalytic oxidation into CO2 and H2O with a 100% conversion rate at temperatures as low as ∼39°C. A catalytic mechanism of the synergistic effect between CeO2 and Co3O4 supports, which greatly accelerates the surface active oxygen migration and activates the Au species, was proposed for explaining the enhanced HCHO catalytic oxidation over 3DOM Au/CeO2-Co3O4 catalysts. The well-controlled method for creation of 3DOM Au/CeO2-Co3O4 catalysts with nanoporous walls could be adopted for generation of other catalytic materials with mixed macroporous and mesoporous structures. The superior catalytic activity of 3DOM Au/CeO2-Co3O4 catalysts makes them potentially applicable to indoor HCHO decontamination and industrial catalysis.
Hierarchical Zeolite Enveloping Pd-CeO2 Nanowires: an Efficient Adsorption/catalysis Bifunctional Catalyst for Low Temperature Propane Total Degradation

Tao Dong,Wenming Liu,Mudi Ma,Honggen Peng,Senyou Yang,Jinxiong Tao,Chi He,Liang Wang,Peng Wu,Taicheng An

DOI: https://doi.org/10.1016/j.cej.2020.124717

IF: 15.1

2020-01-01

Chemical Engineering Journal

Abstract:Volatile organic compounds (VOCs) are significant ozone (O-3) and particulate matter (PM) formation precursors and are deleterious to both human health and environment. Catalytic combustion can degrade VOCs to H2O and CO2 without secondary pollution, suggesting a potential sustainable technology for air pollution control. However, the concentration of exhausted VOCs is usually too low for effective decomposition. Herein, a novel adsorption/catalysis bifunctional catalyst, hierarchical silicalite-1 (S-1) zeolite enveloping Pd-CeO2 nanowires (Pd-CeO2NW@S-1), was designed and prepared using a simple one-pot two-step method and applied for the degradation of propane. Pd-CeO2NW@S-1 exhibited superior catalytic activity (T-90 decreased to 296 degrees C) as well as increased thermal and hydrothermal stability (no obviously decrease in activity when treated at 700 degrees C or reacted with water gas, respectively) compared with Pd-CeO2 nanowires supported on the outer surface of S-1 (Pd-CeO2NW/S-1) and previously reported Pd based catalysts for propane degradation. In addition, the activity over Pd-CeO2NW@S-1 after five reaction cycles just with little decrease and could be restored by a simple regeneration step and without any detection of coke. The remarkable performance over Pd-CeO2NW@S-1 was attributed to the high dispersion of Pd and Ce encapsulated in hierarchical zeolite with superior propane adsorption performance and the special confinement structure according the Mars-van-Krevelen (MvK) mechanism. This confinement adsorption/catalysis bifunctional strategy can be used to design other high-performance catalysts for degradation of VOCs.
Complete oxidation of formaldehyde over a Pd/CeO2 catalyst at room temperature: tunable active oxygen species content by non-thermal plasma activation

Kai Li,Jian Ji,Miao He,Haibao Huang

DOI: https://doi.org/10.1039/d0cy01085e

IF: 3.9

2020-01-01

IEEE Access

Abstract:Formaldehyde is a main indoor pollutant and its removal is essential to protect human health and meet strict environmental regulations. It is highly desirable to develop efficient catalysts to achieve complete oxidation of formaldehyde at room temperature. However the preparation of catalysts generally requires harsh conditions and long times. In this work, a quick, mild and efficient alternative method was employed to prepare a Pd/CeO2 catalyst and adjust its characteristics via non-thermal plasma activation. The plasma activation could obtain tunable active oxygen species content since it can change the metallic Pd percentage, oxygen vacancy concentration and Pd particle size simultaneously. A close relationship between the active oxygen species content and HCHO catalytic oxidation activity was established. The Pd/CeO2 catalyst activated by plasma for only 2 minutes showed the best conversion of over 76% due to its highest active oxygen species amount. The results of in situ DRIFTS of HCHO oxidation over the Pd/CeO2 catalyst suggested that the intermediates mainly included formate, dioxymethylene and polyoxymethylene species. The high content of active oxygen species could promote the rate determining step of formate species oxidation. This study provides a quick and efficient catalyst activation method for HCHO catalytic oxidation at room temperature.
MnCo-Layered double hydroxides nanosheets supported Pd nanoparticles for complete catalytic oxidation of formaldehyde at room temperature

Juanjuan Gong,Xuyu Wang,Haibo W,Xuexue Dong,Jing Li,Fu Yang,Aihua Yuan,Hongbing Ji

DOI: https://doi.org/10.1016/j.apsusc.2022.154702

IF: 6.7

2022-12-30

Applied Surface Science

Abstract:Removal of gaseous formaldehyde by room-temperature catalytic oxidation has promising applications. The rational design of the structure of catalyst to improve the ability of activated key species (adsorbed oxygen and hydroxyl) through understanding the reaction mechanism can improve the catalytic activity. In this paper, Pd nanoparticles were deposited on pre-reduction uniform LDH nanosheets to prepare Pd-decorated sodium borohydride-reduced Mn/Co layered double hydroxides (Pd/LDH-NaBH4). The transition metal (Mn and Co) doping of Pd improved the catalyst's ability to activate oxygen and formaldehyde, and the support of LDHs increased the hydroxyl concentration of the catalyst. Pd/LDH-NaBH4 showed reduced valence of Pd, improved dispersion of Pd NPs, and retention of abundant hydroxyl groups on LDH. Characterizations revealed that the synergistic effect of the supported Pd NPs and LDH, as well as many oxygen vacancies, was responsible for the effective removal of HCHO by Pd/LDH-NaBH4 catalyst at ambient temperature. This study further developed a new catalyst for HCHO oxidation, which may provide a new idea for the removal mechanism of oxidized HCHO.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films
Insight into the Ag-CeO2 Interface and Mechanism of Catalytic Oxidation of Formaldehyde

Guimin Jiang,Yiping Su,Huixia Li,Yafeng Chen,Shun Li,Yibin Bu,Zuotai Zhang

DOI: https://doi.org/10.1016/j.apsusc.2021.149277

IF: 6.7

2021-01-01

Applied Surface Science

Abstract:The interfacial effects between noble metals and supports should be well understood for the design of efficient and low-cost catalysts for HCHO removal. Two Ag/CeO2 catalysts were prepared by using two CeO2 supports with well-defined crystal planes: a nanorod enclosed with the {110} and {100} crystal planes (Ag/CeO2-rod) and commercial CeO2 enclosed with the {111} crystal plane. The reactivity results demonstrated that Ag/CeO(2)rod was a highly efficient active catalyst, which completely oxidized HCHO at 80 degrees C Compared to commercial CeO2, CeO2 nanorod had more oxygen vacancies and surface-active oxygen species, which were further promoted by the Ag-CeO2 interface. The HCHO could be quickly adsorbed and oxidized at the Ag-CeO2 interface, which led to the high reactivity for HCHO oxidation. This article not only proposes the reaction mechanism of HCHO oxidation but also provides ideas for the design of additional highly efficient and low-cost catalysts.
Promoted oxygen adsorption on porous CeO2 cubes with abundant oxygen vacancies for efficient gaseous formaldehyde removal

KangYi Zhang,QiuRuo Pu,JinYuan Wang,Demin Li,Lei Xu,MingZheng Xie,Jing Cao

DOI: https://doi.org/10.1016/j.chemosphere.2024.142576

IF: 8.8

Chemosphere

Abstract:Photocatalytic degradation stands as a promising method for eliminating gas-phase pollutants, with the efficiency largely hinging on the capture of photogenerated electrons by oxygen. In this work, we synthesized a porous CeO2 single crystal cube with abundant oxygen vacancies as photocatalyst, employing urea as a pore-forming agent and for gas-phase formaldehyde degradation. Compared with the CeO2 cubes without pores, the porous ones were superior in specific surface area, akin to conventional CeO2 nanoparticles. The photocatalytic degradation for gas-phase formaldehyde on porous CeO2 cubes was significantly accelerated, of which degradation rate is 3.3 times and 2.1 times that of CeO2 cubes without pores and CeO2 nanoparticles, respectively. Photoelectric tests and DFT calculations revealed that this enhancement stemmed from facilitated oxygen adsorption due to pronounced oxygen vacancies. Consequently, the capture of photoelectrons by oxygen was promoted and its recombination with holes was suppressed, along with an accelerated generation of curial free radicals such as ·OH. This work reveals the pivotal role of surface oxygen vacancies in promoting adsorbed oxygen, proposing a viable strategy to enhance the photocatalytic degradation efficiency for gas-phase pollutants.
Electrospinning synthesis of Co 3 O 4 porous nanofiber monolithic catalysts for the room-temperature indoor catalytic oxidation of formaldehyde at low concentrations

Yujun Jiao,Cha Jing,Yuqin Wang,Fan Yao,Guangzheng Ye,Xiaohong Wang,Guangyi Zhao,Weixiao Peng,Haomin Huang,Daiqi Ye

DOI: https://doi.org/10.1016/j.apsusc.2023.158215

IF: 6.7

2023-08-13

Applied Surface Science

Abstract:Room-temperature catalytic oxidation is a highly promising method for controlling formaldehyde (HCHO) concentrations indoors because it does not require any additional energy input, while completely converting HCHO into harmless H 2 O and CO 2 . This study focuses on the synthesis of Co 3 O 4 porous nanofiber monolithic catalysts through electrospinning and investigates the mechanism behind the formation of its porous structure by analyzing the morphological changes that occur during the calcination of its fibers. In this research, we utilized heat-resistant polyacrylonitrile (PAN) as template to synthesize Co 3 O 4 porous nanofiber monolithic catalysts. The synthesis process involved the utilization of the oxidation characteristics of PAN in the presence of cobalt acetate tetrahydrate (CH 3 COO) 2 Co·4H 2 O at 270–330 °C. Co 3 O 4 porous nanofiber monolithic catalyst demonstrated exceptional performance, exhibiting over 99% catalytic activity toward HCHO at room-temperature in indoors (10–12 ppm, 25 °C) at a gas hourly space velocity of 60,000 mL·g −1 h −1 . This catalyst demonstrates its suitability for practical applications and its potential for energy savings. These results highlight the superiority of Co 3 O 4 porous nanofiber monolithic catalyst over catalysts produced via the direct calcination method. The outstanding activity and stability of Co 3 O 4 porous nanofiber monolithic catalyst make it a promising candidate for applications requiring efficient formaldehyde removal, particularly in indoors.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films
Low Cost and Highly Dispersed Ce/Na-ZSM-5 Catalysts Close to Atomic Dispersion for Enhancing Formaldehyde Oxidation.

Zhihao Xu,Kai-Hang Ye,Yuying Zheng,Zhiting Liang,Tongxin Tang,Ying Zhang,Xiaohui He,Hongbing Ji

DOI: https://doi.org/10.1039/d3dt00403a

IF: 4

2023-01-01

Dalton Transactions

Abstract:Formaldehyde oxidation at room temperature with low-cost catalysts is one of the main development directions of environmental governance. Herein, we developed a low-cost and superior performance highly dispersed Ce on Na-ZSM-5 (Ce/Na-ZSM-5) catalyst, which is close to atomic dispersion for indoor formaldehyde (HCHO) oxidation at low temperature. The highly dispersed catalyst that was similar to atomic dispersion was characterized by EXAFS and AC HAADF-STEM. The optimal Ce/Na-ZSM-5 displays high HCHO removal performance (95%, at room temperature), as well as 100 h stable testing (∼90% HCHO removal). In addition, a reasonable reaction mechanism of the HCHO catalytic oxidation is proposed based on the in situ DRIFT spectra and DFT calculation. This work provides a new way to design an efficient catalyst for the complete oxidation of formaldehyde.
Investigation of formaldehyde oxidation over Co3O4-Ce2 and Au/Co3O4-CeO2 catalysts at room temperature: effective removal and determination of reaction mechanism

Chunyan Ma,Donghui Wang,Wenjuan Xue,Baojuan Dou,Hailin Wang,Zhengping Hao

DOI: https://doi.org/10.1021/es104146v

2011-04-15

Abstract:Formaldehyde is regarded as the major indoor pollutant emitted from widely used building and decorative materials in airtight buildings, which should be eliminated under indoor environmental conditions. We report here catalytic oxidation process of formaldehyde over mesoporous Co(3)O(4), Co(3)O(4)-CeO(2), Au/Co(3)O(4), and Au/Co(3)O(4)-CeO(2) catalysts and their excellent catalytic performances at room temperature. These catalysts were prepared by a "nanocasting" method with the mesostructure generated from SBA-15 silica with 2D structure. The adsorbed surface species in the formaldehyde oxidation process are analyzed, and some key steps in the oxidation pathway, active sites, and intermediate species are proposed. Among the detected species, some kinds of formate species formed on the catalysts were indentified as intermediates, which further transformed into bicarbonate or carbonate and which decomposed to carbon dioxide. The role of the mesoporous Co(3)O(4) and the gold nanoparticles in the mechanism are also revealed.

Fabrication of Pd/CeO 2 nanocubes as highly efficient catalysts for degradation of formaldehyde at room temperature

High Surface Area Au/CeO2 Catalysts for Low Temperature Formaldehyde Oxidation

Highly efficient formaldehyde elimination over meso-structured M/CeO2 (M = Pd, Pt, Au and Ag) catalyst under ambient conditions

Efficient Removal Of Formaldehyde By Nanosized Gold On Well-Defined Ceo2 Nanorods At Room Temperature

Highly dispersed Fe-Ce mixed oxide catalysts confined in mesochannels toward low-temperature oxidation of formaldehyde

Efficient activation of Pd/CeO2 catalyst by non-thermal plasma for complete oxidation of indoor formaldehyde at room temperature

One-step fabrication of Pd-embedded hierarchically porous carbon micro-spheres for formaldehyde removal under mild conditions

Construction of strongly-coupled CeO 2 /MnO 2 heterogeneous catalysts for highly-efficient removal of formaldehyde

The composite of UiO-66 derived ZrO2 and g-C3N4 for oxidative removal of formaldehyde at the room temperature

Ag/Ceo2 Nanospheres: Efficient Catalysts for Formaldehyde Oxidation

Photocatalytic Degradation of Gaseous Formaldehyde by Fe-Doped ZnO Nanorods Grown on Ceramic Spheres

Preparation of porous MnO2/CeO2 composite for the effective removal of formaldehyde from air

Three-dimensionally ordered macroporous Au/CeO 2-Co 3O 4 catalysts with nanoporous walls for enhanced catalytic oxidation of formaldehyde

Hierarchical Zeolite Enveloping Pd-CeO2 Nanowires: an Efficient Adsorption/catalysis Bifunctional Catalyst for Low Temperature Propane Total Degradation

Complete oxidation of formaldehyde over a Pd/CeO2 catalyst at room temperature: tunable active oxygen species content by non-thermal plasma activation

MnCo-Layered double hydroxides nanosheets supported Pd nanoparticles for complete catalytic oxidation of formaldehyde at room temperature

Insight into the Ag-CeO2 Interface and Mechanism of Catalytic Oxidation of Formaldehyde

Promoted oxygen adsorption on porous CeO2 cubes with abundant oxygen vacancies for efficient gaseous formaldehyde removal

Electrospinning synthesis of Co 3 O 4 porous nanofiber monolithic catalysts for the room-temperature indoor catalytic oxidation of formaldehyde at low concentrations

Low Cost and Highly Dispersed Ce/Na-ZSM-5 Catalysts Close to Atomic Dispersion for Enhancing Formaldehyde Oxidation.

Investigation of formaldehyde oxidation over Co3O4-Ce2 and Au/Co3O4-CeO2 catalysts at room temperature: effective removal and determination of reaction mechanism