Abstract:In order to achieve desired mechanical properties of alloys by manipulating grain boundaries (GBs) via solute decoration, it is of great significance to understand the underlying mechanisms of microstructural evolution and plastic deformation. In this work, nanocrystalline (NC) Cu-W alloyed films with W concentrations spanning from 0 to 40 at% were prepared by using magnetron sputtering. Thermal stability (within the temperature range of 200 °C-600 °C) and hardness of the films were investigated by using the x-ray diffraction, transmission electron microscope (TEM) and nanoindentation, respectively. The NC pure Cu film exhibited substantial grain growth upon all annealing temperatures. The Cu-W alloyed films, however, displayed distinct microstructural evolution that depended not only on the W concentration but also on the annealing temperature. At a low temperature of 200 °C, all the Cu-W alloyed films were highly stable, with unconspicuous change in grain sizes. At high temperatures of 400 °C and 600 °C, the microstructural evolution was greatly controlled by the W concentrations. The Cu-W films with low W concentration manifested abnormal grain growth (AGG), while the ones with high W concentrations showed phase separation. TEM observations unveiled that the AGG in the Cu-W alloyed thin films was rationalized by GB migration. Nanoindentation results showed that, although the hardness of both the as-deposited and annealed Cu-W alloyed thin films monotonically increased with W concentrations, a transition from annealing hardening to annealing softening was interestingly observed at the critical W addition of ∼25 at%. It was further revealed that an enhanced GB segregation associated with detwinning was responsible for the annealing hardening, while a reduced solid solution hardening for the annealing softening.

Effect of W concentration on the thermal stability of Cu-carbon nanotube hybrids

The Effect of A Small Amount of Tungsten on the Microstructure of Mechanically Alloyed Ag37cu63

The W alloying effect on thermal stability and hardening of nanostructured Cu-W alloyed thin films

Effect of Al2O3 coating thickness on the thermal stability of Cu–carbon nanotube hybrids

Atomic Scale Stability of Tungsten-Cobalt Intermetallic Nanocrystals in Reactive Environment at High Temperature.

Influences of Carbon Nanotubes on Performance of W-Cu Composite Materials

Ultrahigh thermal stability of carbon encapsulated Cu nanograin on a carbon nanotube scaffold

Thermal Stability of Carbon Nanotubes Probed by Anchored Tungsten Nanoparticles

Ultrahigh strength, thermal stability and high thermal conductivity in hierarchical nanostructured Cu-W alloy

Effect of carbon nanotube content and annealing temperature on corrosion performance of carbon nanotube/Ni composite layer

Study on the Mechanism of CNTs Regulating the Microstructures and Properties of Al–Cu–Mg Alloy

Effect of Carbon Nanotubes and High Temperature Extrusion on the Microstructure Evolution of Al-Cu Alloy

The High Thermal Stability Induced by a Synergistic Effect of ZrC Nanoparticles and Re Solution in W Matrix in Hot Rolled Tungsten Alloy

Regulating the interfacial reaction between carbon nanotubes and aluminum via copper nano decoration

Effect of Crystallinity on the Field Emission Characteristics of Carbon Nanotube Grown on W-Co Bimetallic Catalyst

Remarkable improvement of wettability of Cu-coated carbon nanotubes by molten aluminum

Thermal Transport Across Cu-Metal-Carbon Nanotube Interfaces Enhanced by Effective Interfacial Interaction

Enhancing mechanism of CNT-CNT interface by metal nanoparticle and nanowire effect on the inside and outside of CNT

Effect of Carbon Nanotube (CNT) Content on the Properties of In-Situ Synthesis CNT Reinforced Al Composites

Enhanced nanocrystalline stability of BCC iron via copper segregation

Enhanced electrical conductivity and hardness of Copper/Carbon Nanotubes composite by tuning the interface structure