Abstract:Nitinol (NiTi) is an intermetallic compound and a member of the shape memory alloy family. This widely used material has unique properties such as biocompatibility, superelasticity, good corrosion resistance, and abrasion resistance, which distinguish it from the other shape memory materials. The most common applications of this alloy in medical engineering are in the manufacture of orthodontic wires, orthopedic implants, and guide wires in cardiovascular surgery. The production of orthopedic implants requires porous structures and bone-like tissue. In the present study, sodium chloride, polystyrene beads, and sawdust were used as space holder during the combustion synthesis process to produce porous NiTi alloy. The effect of space holder type on the percentage, distribution, and size of porosity of the synthesized samples were investigated. The sample's porosity percentage without the space holder was 30% and increased to 52, 36, and 37% by using sodium chloride, polystyrene beads, and sawdust spacers, respectively. The microstructure and phases of the specimens were examined using scanning electron microscopy (SEM) equipped with x-ray energy diffraction (EDS) spectroscopy and x-ray diffraction (XRD) analysis in samples with NaCl space holders with higher percentages and more controlled porosity. The microstructure of the synthesized sample without the space holder consisted of NiTi, NiTi 2 , Ni 3 Ti, and Ni 4 Ti 3 , and the addition of the sodium chloride did not change the phases. The Young's modulus and compressive strength of the synthesized sample without a space holder were 0.4 GPa and 59.7 MPa, respectively, which decreased with the addition of sodium chloride particles to 0.2 GPa and 25.5 MPa.

Self-exothermic Reaction Behavior and Pore Structures of Ni-Al Intermetallics with More than 70% Porosity

Preparation of Porous NiAl Intermetallic with Controllable Shape and Pore Structure by Rapid Thermal Explosion with Space Holder

Effect of the heating rate on the thermal explosion behavior and oxidation resistance of 3D-structure porous NiAl intermetallic

A Reaction Study for Al–Ni2O3 Nano Self-Exothermic Materials

Pore structures of high-porosity NiTi alloys made from elemental powders with NaCl temporary space-holders

Reaction mechanism and oxidation resistance at 700–900 °C of high porosity NiAl intermetallic

Progress of porous Al-containing intermetallics fabricated by combustion synthesis reactions: a review

High Porosity and High-Strength Porous NiTi Shape Memory Alloys with Controllable Pore Characteristics

Fabrication and Characterization of Highly Porous FeAl-Based Intermetallics by Thermal Explosion Reaction

Preparation of High-Porosity Niti Alloys by Powder Sintering with Nacl Pre-Forming

Preparation and properties of FeNiMnCuC0.2Alx high-entropy alloy

Highly Porous Co-Al Intermetallic Created by Thermal Explosion Using NaCl as a Space Retainer

Preparation and Properties of Porous Superalloy Materials with Hollow Spherical Pores

Fabrication of Porous FeAl-based Intermetallics Via Thermal Explosion

Gradient Porosity and Large Pore Size NiTi Shape Memory Alloys

Pore Control in Porous NiTi Alloy Produced by Combustion Synthesis Method with the Utilization of Space Holders

Microstructure and Mechanical Properties of Porous NiTi Alloy Prepared by Integration of Gel-Casting and Microwave Sintering

Preparation of Controllable Porous Ti–Al Materials with Zn Space Holders

Microstructure and formation mechanism of Ni-Al intermetallic compounds fabricated by reaction synthesis

Fabrication of Porous Aluminum with Controllable Open-Pore Fraction

Space-holder engineered porous NiTi shape memory alloys with improved pore characteristics and mechanical properties