Fabrication of Porous Zn Alloy Scaffolds Coated with Hydrophobic Film and Their In Vitro Biodegradation Properties

Donghui Yang,Xia Hong,Jianqing Chen,Hui He,Lei Wang

DOI: https://doi.org/10.1007/s11837-024-06667-3

2024-06-07

JOM

Abstract:Porous Zn scaffold, as a novel biodegradable metallic material, has emerged as a promising candidate for biomedical applications. In this paper, by using carbamide particles as the pore-making agent and Zn and Mg powders as the starting materials, porous Zn-Mg alloy scaffolds were fabricated via the low-temperature sintering route. A so-called one-step hydrothermal method was applied to form a hydrophobic film on surface of the porous Zn alloy scaffolds. The degradability of the porous Zn alloy scaffolds coated with/without hydrophobic film in the simulated body fluid (SBF) was investigated, and the results show that the hydrophobic film, which can adhere well to the metal substrate with thickness around 50 μm, can effectively delay the degradation of porous Zn alloy scaffolds; the degradation rates of porous Zn alloy scaffolds coated by the hydrophobic film are 26–57% lower than those of porous scaffolds without coating; especially the degradation rate of the porous Zn-5 wt.%Mg scaffold with the coating in SBF, which is 0.32 mg/(cm 2 day), is at the same level as that of pure Zn.

materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy